研究了采用铅锌尾矿和页岩配制的高C3S硅酸盐水泥生料的易烧性及所得熟料的性能.设计了18个熟料组成并分别在1350℃,1400℃,1450℃和1500℃下进行煅烧,对所得熟料作游离氧化钙及X射线衍射测试.结果表明1500℃下可以制备出C3S含量达74.52%的熟料.在工业回转窑正常煅烧温度下烧成了C3S含量达70.71%的熟料.部分熟料中加入4%的石膏制得水泥,其性能符合强度等级52.5R的硅酸盐水泥标准要求.加入20%尾矿粉后水泥可满足普通水泥42.5R的强度要求,掺加30%尾矿粉后水泥可达到普通水泥32.5R的强度要求.
参考文献
| [1] | 陈益民,郭随华,管宗甫.高胶凝性水泥熟料[J].硅酸盐学报,2004(07):873-879. |
| [2] | 侯贵华,沈晓冬,许仲梓.高硅酸三钙硅酸盐水泥熟料组成及性能的研究[J].硅酸盐学报,2004(01):85-89. |
| [3] | Tsuboi T;Ito T;Hokinoue Y et al.The effect of MgO,SO3 and ZnO on the sintering of Portland cement clinker[J].Zement-Kalk-Gips,1972,25(09):426-431. |
| [4] | Zhong Jingyu;Yang Jiazhi;Xu Youhong.The effect of ZnO-doped on the properties of alite[A].北京,1989:192-199. |
| [5] | Xu G L;Huang W X;Lu Z Y.The effect of ZnO on burning of Portland cement clinker in rapid heating-up burning[A].New Delhi,India,1992:372-378. |
| [6] | Kakali G;Parissakis G .Investigation of the effect of Zn oxide on the formation of Portland cement clinker[J].Cement and Concrete Research,1995,25(01):79-85. |
| [7] | Murat M;Sorrentino F .Effect of large additions of Cd,Pb,Cr,Zn,to cement raw meal on the composition and the properties of the clinker and cement[J].Cement and Concrete Research,1996,26(03):377-385. |
| [8] | Kakali G;Parissakis G;Bouras D .Study on the burnability and the phase formation of PC clinker containing Cu oxide[J].Cement and Concrete Research,1996,26(10):1473-1478. |
| [9] | K. Kolovos;S. Tsivilis;G. Kakali .The effect of foreign ions on the reactivity of the CaO-SiO_2-Al_2O_3-Fe_2O_3 system Part II: Cations[J].Cement and Concrete Research,2002(3):463-469. |
| [10] | 刘晓存,李艳君,单连梅.ZnO和CaF2对C3S和C4A3S矿物形成的影响[J].建筑材料学报,2003(01):9-12. |
| [11] | 管宗甫,陈益民,秦守婉.杂质离子对硅酸盐水泥熟料烧成影响的研究进展[J].硅酸盐学报,2003(08):795-800. |
| [12] | 崔素萍,兰明章,张江,王彩云.废弃物中重金属元素在水泥熟料形成过程中的作用及其固化机理[J].硅酸盐学报,2004(10):1264-1270. |
| [13] | 管宗甫;张素芳;杨久 等.铅锌尾矿作为水泥熟料煅烧矿化剂的研究[J].郑州大学学报(自然科学版),1998,30(01):28-32. |
| [14] | 周元林,谢华,卢忠远.利用工业副产物制备硅酸盐水泥熟料[J].中国水泥,2003(06):18-20. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%