以BaCl2、TiCl4为原料,以(NH4)2C2O4·H2O为沉淀剂,利用微波-沉淀法制备了高纯四方相钛酸钡纳米粉体.应用XRD、TEM等对粉体的结构、形貌进行了分析.研究表明,微波-沉淀法合成粉体的时间为50 min,制备的粉体属于四方相晶体结构,粒度为30nm、粒度分布均匀,杂质含量达到电子行业工业标准.
参考文献
| [1] | Hilton A D;Frost R .Resent developments in the manufacture of barium titanate powders[J].Key Engineering Materials,1992,66:145-184. |
| [2] | Viswanasth R N;Ramasamy S .Preparation and ferroelectric phase transition studies of nano-crystalline BaTiO3[J].Nano-Structured Materials,1997,8(02):155-162. |
| [3] | Pascal Pinceloup;Christian Courtois;Anne Leriche;Bernard Thierry .Hydrothermal synthesis of nanometer-sized barium titanate powders: control of barium/titanium ratio, sintering, and dielectric properties[J].Journal of the American Ceramic Society,1999(11):3049-3056. |
| [4] | Her Y S;Matijevic E;Chon M C .Preparation of well-defined colloidal barium titanate crystals by the controlled double jet precipitation[J].Materials Research,1995,101(12):3106-3114. |
| [5] | 徐华蕊,高濂,郭景坤.水热合成高纯四方相钛酸钡纳米粉末研究[J].功能材料,2001(05):558-560. |
| [6] | 全学军,李大成.共沉淀法制备钛酸钡微粉的研究[J].无机材料学报,2001(05):853-860. |
| [7] | Baghurst D R;Cgippirdate A M .Microwave syntheses for superconducting ceramics[J].Nature,1988,332:331. |
| [8] | 刘韩星;李永伟;张汉林 等.BaTiO3微波合成的反应机理研究[J].中国科学A辑,1998,27(04):350-356. |
| [9] | 李永伟;刘韩星;张汉林 等.微波合成BaTiO3加热机制及反应产物的显微结构研究[J].中国科学A辑,1998,27(02):146-150. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%