研究了化学合成高纯铝酸钙水泥的物理特性,包括强度发展、凝结时间、水化结合水量和水化放热特性,并与市售的以传统烧结法生产的水泥进行了在典型耐火浇注料中的应用比较.结果表明:(1)化学合成高纯铝酸钙水泥胶砂的强度发展快且充分,早期强度高;(2)化学合成高纯铝酸钙水泥的水化放热速率在水化2 h时最大,放热快且放热量集中;(3)化学合成高纯铝酸钙水泥的水化活性较高;(4)化学合成纯铝酸钙水泥用于耐火浇注料中,浇注料表现出较高的烘干强度,且浇注料的烧后强度等性能指标也与用传统烧结水泥的大体相当.
参考文献
| [1] | Fujii K;Kondo W .Kinetic of hydration of monocalcium aluminates[J].Journal of the American Ceramic Society,1986,69(04):361-364. |
| [2] | Singh V K;Ali M M .Formation kinetics of calcium aluminates[J].Journal of the Australian Ceramic Society Series A,1990,73:872-876. |
| [3] | Song T W;Choi S H;Han Kan K S.Calcium aluminates cements[M].London,1998:9-11. |
| [4] | 秦景燕,王玉江,任和平,汪开泰.低温烧成纯铝酸钙水泥的机理研究[J].硅酸盐通报,2002(03):51-54,58. |
| [5] | Morozova L P .Preparation of calcium aluminates by a chemical method[J].Cement and Concrete Research,1988,18:375-388. |
| [6] | Mehmet A Gulgun;Oludele O Popoola .Chemical synthesis and characterization of calcium aluminate powders[J].Journal of the American Ceramic Society,1994,77(02):531-539. |
| [7] | 陈峰,洪彦若,孙加林,卜景龙,李玉山.高纯铝酸钙粉体的化学合成[J].耐火材料,2004(04):245-248. |