用感应炉浸渍试验法(熔池温度1650 ℃左右,侵蚀时间20 min)研究了V2O5含量分别为0、1.34%、2.0%、3.15%的钢渣对镁碳砖的侵蚀.结果表明:由于V2O5降低了渣的熔化温度与粘度,含钒钢渣对镁碳砖的侵蚀性明显高于不含钒的普通钢渣,随渣中V2O5含量由0增加到3.15%,镁碳砖的熔损指数由14.3%上升到42.9%,渗透深度比采用普通钢渣时提高1.2倍.渣中V2O5和TiO2随液相渗入砖中,一部分与基质中的碳反应,导致碳的氧化和MgO颗粒在渣中的溶解;另一部分则侵入MgO晶界中肢解镁砂,使骨料破坏,加速对MgO-C砖的破坏.
参考文献
| [1] | W. E. Lee;S. Zhang .Melt corrosion of oxide and oxide-carbon refractories[J].International Materials Reviews,1999(3):77-104. |
| [2] | K Tabata;H Nishio;K Itoh .Study on oxidation-reduction reaction in MgO-C refractory[J].Taikabutsu Overseas,1988,8(04):3-10. |
| [3] | S Zhang;A Yamaguchi .Effects of CaO and Al2O3 added to MgO-C refractories on MgO-C reaction[J].Journal of the Ceramic Society of Japan,1996,104(02):84-88. |
| [4] | 陈肇友;吴学真;叶方保.转炉中钒钛铝氧化物对MgO-CaO系材料的侵蚀[A].北京:冶金工业出版社,1998:175-187. |
| [5] | Ronald A McCauley.The effects of Vanadium upon basic refractory[A].American Society Ceramic,Westerville,OH,1989:858-863. |
| [6] | Parker F J;McCauley R A .Investigation of the system CaO-MgO-V2O5(Ⅱ),Phase Equilibria[J].Journal of the American Ceramic Society,1982,65(07):349-351. |
| [7] | 王诚训.MgO-C质耐火材料[M].北京:冶金工业出版社,1995 |
| [8] | 宋国才;汤天宇;陈小武.镁碳砖在攀钢氧气转炉上使用损毁原因分析[J].攀钢技术,1995(02):26-31. |
| [9] | 叶大伦;胡建华.实用无机物热力学数据手册[M].北京:冶金工业出版社,2002 |
| [10] | 刘刚.氧气转炉含钒炉渣相图及一些氧化物对CaO-FeO-SiO2渣系性能的影响[J].北京钢铁学院学报,1983(01):21-42. |
| [11] | 文永才.含V2O5、TiO2钢渣熔化性质的研究[J].钢铁,2002(09):17-19,34. |
| [12] | 孔繁芬 .含钒钢渣粘度研究[R].,1979. |
| [13] | 陈家祥.炼钢常用图表数据手册[M].北京:冶金工业出版社,1984:214. |
| [14] | 董履仁 .含钒转炉渣与碱性耐火材料的作用机理[R].,1980. |
| [15] | 万新,裴鹤年,白晨光,周培土.钛氧化物还原与钛渣变稠[J].重庆大学学报（自然科学版）,2000(05):36-39,61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%