为了改善Al2O3-C质耐火材料的抗氧化性和抗热震性,向浇注料中分别添加0、2%、4%、6%的SiC或ZrO2-SiC复合粉,以酚醛树脂为结合剂,在200 MPa下制备了2组试样,经250 ℃充分干燥后,于1 400 ℃下埋炭处理2 h,分别检测2组试样的抗氧化性和抗热震性,并采用XRD分析氧化后试样的相组成.结果发现,添加剂中SiC的氧化能有效保护试样中的碳,从而能减少试样的质量损失率和氧化面积,提高其抗氧化性能.由于ZrO2的微裂纹增韧及SiC的颗粒增韧作用,使试样的抗热震性能提高.在试验条件下,添加6%ZrO2-SiC复合粉或工业SiC粉时,试样的抗氧化性和抗热震性最佳.
参考文献
| [1] | Chan CF.;Lee WE.;Argent BB. .Influence of additives on slag resistance of Al2O3-SiO2-SiC-C refractory bond phases under reducing atmosphere[J].Journal of the American Ceramic Society,1998(12):3177-3188. |
| [2] | Yamaguchi A .Behaviors of SiC and Al added to carbon containing refractories[J].Taikabutsu Overseas,1984,4(03):14-18. |
| [3] | Sun Y;Yu J K .Effects of B4C and SiC additions on properties of alumina-graphite refractories[J].China's Refractories,2007,16(zk):177-179. |
| [4] | Yu J K;Hiragushi K .Synthesis of Al2O3-SiC composite from pyrophyllite and clay and its application in carbon-containing refractories[J].Taikabutsu Overseas,1998,19(02):11-17. |
| [5] | 于景坤,戴文斌,戴淑平.赛隆-碳化硅系复合材料的合成及其应用[J].东北大学学报(自然科学版),2003(09):824-827. |
| [6] | 马北越,于景坤,谭诚.碳热还原锆英石合成ZrO2-SiC复合材料[J].耐火材料,2007(04):252-254. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%