以连云港市东海蛇纹石粉为主要原料，辅以α-Al2 O3和石英粉高温合成堇青石，分别配成符合理论组成的配方，SiO2质量分数比理论组成分别多5和10百分点的配方，以及Al2 O3质量分数比理论组成分别多5和10百分点的配方，经球磨、造粒、烘干、冷等静压成型后，分别在1050、1100、1150、1200和1250℃保温2 h，然后检测试样的显气孔率、体积密度和常温抗折强度，并进行XRD和SEM分析。结果表明：合成的堇青石呈较完整的六方柱状形貌；增大石英粉的添加量能降低材料的合成温度，制得致密度较高的堇青石材料；增大α-Al2 O3添加量，合成的堇青石气孔较多，结构疏松。
Cordierite was prepared at high temperatures using serpentine powder from Donghai Lianyunga-ng as the main starting material,adding α-Al2 O3 and quartz powder.Five formulations were adopted:stoi-chiometric,SiO2 addition 5% or 10% higher than the stoichiometric,and Al2 O3 addition 5% or 10% higher than the stoichiometric.The batched materials were ball milled,granulated,dried,cold isostatic pressed and fired at 1 050,1 100,1 150,1 200,and 1 250 ℃for 2 h,respectively.The apparent porosity,bulk density and cold modulus of rupture of the prepared specimens were tested,and specimens were analyzed by XRD and SEM.The results show that the synthesized cordierite has a complete hexagonal columnar mor-phology;increasing quartz powder addition reduces the synthesis temperature,obtaining denser cordier-ite;increasing α-Al2 O3 addition leads to porous cordierite with a loose structure.
参考文献
| [1] | 段满珍,杨立荣,黄转红.合成堇青石材料的烧成制度研究[J].耐火材料,2011(04):285-287. |
| [2] | Goren R;Gocmez H;Ozgur C .Synthesis of cordierite powder from talc,diatomite and alumina[J].CERAMICS INTERNATIONAL,2006,32(04):407-409. |
| [3] | A.Yamuna;S.Honda;K.Sumita;M.Yanagihara;S.Hashimoto .Synthesis,sintering and thermal shock resistance estimation of porous cordierite by IR heating technique[J].Microporous and Mesoporous Materials,2005(1/2):169-175. |
| [4] | 白建光,赵敬忠.莫来石含量对堇青石-莫来石复相陶瓷性能的影响[J].耐火材料,2008(05):365-367. |
| [5] | Yamuna A;Johnson R;Mahajan Y R et al.Kaolin-based cordierite for pollution control[J].Journal of the European Ceramic Society,2004,24(01):65-73. |
| [6] | Acimovic Z;Pavlovic L;Trumbulovic L et al.Synthesis and charac-terization of the cordierite ceramics from nonstandard raw materials for application in foundry[J].Materials Letters,2002,57(18):2651-2656. |
| [7] | 周燕,徐晓虹.累托石合成堇青石研究[J].非金属矿,2004(04):12-13,15. |
| [8] | 胡宾生,熊飞武.蛇纹石种类和粒度对烧结过程的影响[J].烧结球团,2010(05):23-26. |
| [9] | 杨志宽 .蛇纹石粉矿综合利用研究[J].环境科学进展,1997,5(02):32-36. |
| [10] | 于龙泉,王杰曾,汪澜,考宏涛,杨圣玮.堇青石对镁铝尖晶石质耐火材料抗热震性能的影响[J].硅酸盐通报,2012(04):935-938. |
| [11] | Wen-Juan Li;Zhao-Hui Huang;Yan-Gai Liu;Ming-Hao Fang;Xin Ouyang;Sai-Fang Huang .Phase behavior of serpentine mineral by carbothermal reduction nitridation[J].Applied clay science,2012(Mar.):86-90. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%