采用X射线、荧光光谱化学分析XRF、场发射扫描电镜FESEM、能谱分析EDS、X射线衍射XRD以及KMnO4溶液滴定等方法，对一种市售电熔铁铝尖晶石原料进行了分析。结果显示：该原料并不是纯的FeAl2 O4，其主晶相为Fe（Al，Fe）2 O4型固溶体，与磁铁矿型固溶体共生；次晶相为β-Al2 O3，由氧化铝原料中的Na2 O所致。
A commercial fused hercynite material was analyzed by X-ray fluorescence spectrometry (XRF), field emission scanning electron microscope(FESEM),energy dispersive spectroscopy(EDS),X-ray dif-fraction (XRD)and KMnO4 solution titration,etc.The results show the material is not pure FeAl2 O4;the main crystalline phase is Fe(Al,Fe)2O4-type solid solution,symbiosing with magnetite-type solid solution;the secondary crystalline phase is β-Al2O3,which is caused by Na2O in the Al2O3 material.
参考文献
| [1] | Buchebner G;Harmuth H;Molinari T.Magnesia-Hercynite bricks-an innovative burnt basic refractory[A].Berlin,Germany,1999:201-203. |
| [2] | 刘会林,沈建萍,刘雄章,李宁,沈卫平.水泥窑烧成带用镁铁铝尖晶石砖的研制[J].耐火材料,2004(06):414-416. |
| [3] | 陈俊红,封立杰,孙加林,封吉圣,朱波.铁铝尖晶石的合成及镁铁铝尖晶石砖的性能与应用[J].耐火材料,2011(06):457-461. |
| [4] | 周勇,李楠.镁砂与电熔合成铁铝尖晶石-刚玉复合材料的反应[J].耐火材料,2010(06):419-422. |
| [5] | McIntosh A B;Rait J R;Hay R.The binary system FeO-Al2 O3[J].Roy Tech Coll Glasgow J,1937(04):72-76. |
| [6] | Fischer W A;Hoffmann A .Das zustandsschaubild eisenoxydul-alu-miniumoxyd[J].Arch Eisenhuettenwes,1956,27(05):343-346. |
| [7] | Novokhatskii I A;Belov B F;Gorokh A V et al.The phase diagram for the system ferrous oxide-alumina[J].Russian Journal of physical chemistry,1965,39(11):1498-1500. |
| [8] | Rosenbach K;Schmitz J A .Ternary system iron (Ⅱ)oxide-chromi-um (Ⅲ)oxide-alumina[J].Arch Eisenhuettenwes,1974,45(12):843-847. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%