总结了激光熔敷陶瓷涂层的特点,分析了熔敷陶瓷涂层存在的问题,并阐述了自生陶瓷涂层的优点.

参考文献

[1] Molian P A .Hualun L Laser cladding of Ti-6Al-4V with BN for improved wear performance[J].Wear,1989,130(02):337-352,0043-1648.
[2] Zhou X B;De Hosson J T M.A reaction coating on alwminium alloy by laser proccessing[J].Screen,1993(28):219.
[3] Vande E;Haar Modian P A.[A].,1987
[4] 陈传忠;王文中;张建新 .45钢表面激光熔敷陶瓷涂层的研究[J].金属学报,1999,35(09):889-994.
[5] Ariely S;Shen J;Bamberger M et al.Laser surface alloying of steel with TiC[J].Surface and Coatings Technology,1991,45(1/3):403-408.
[6] Fasasi A Y;Pons M;Tassin C.Laser surface melting of mild steel with submicronic titanium carbice powders[J].Journal of Materials Science,1994(29):5121-5126.
[7] 周二华;曾晓雁;吴新伟 等.A3钢表面激光熔敷Fe-WC金属陶瓷复合层的研究[J].激光技术,1997,21(01):34-37.
[8] 刘志勤;王开富 .激光熔敷金属陶瓷复合合金层的组织与性能研究[J].激光技术,1998,22(01):46.
[9] Monanty P S;Gruzleski JE .Grain retinement of aluminium by TiC[J].Screen,1994,31(02):179.
[10] Jasmin K M;Rawlings, R D;West D R F .Metal-ceramic functionally gradient material produced by laser processing[J].Materials Science,1993,28(10):2820-2826.
[11] 刘江龙;邹至荣 等.激光产生金属表层合金化的若干问题[J].应用激光,1988,8(03):129-140.
[12] Ayers. J D.Particulute-TiC-Hardened street surface modification[A].,1983
[13] Chen Y;Chunng D D L .ln Situ Ai-TiB Composite Obtained by Stir Casting[J].Materials Science,1996,31(02):311-315.
[14] Pai B C;Ramani G;Pillai R M et al.Satyanarayana, Role of Magnesium in Cast Aluminium Alloy Composites[J].Materials Science,1995,30(08):1903-1911.
[15] Takalo Choh;Makoto Kobashi;Hiromichinakata et al.FabricationofMetal Matrix Composite by Spontaneous Infiltrationd Subsequent In situ Reaction Process[J].Materials Science Forum,1996,217~222(01):353358.
[16] WANG Z;Li Q;Li C et al.Microstructure and Properties ofIn -Situ TiC Pariculate Reinforeed Al-Si Alloy Composite[J].Acta metall. Sinica,1994,30(01):B39-44.
[17] 张松,张春华,吴维,王茂才.Ti6Al4V表面激光熔覆原位自生TiC颗粒增强钛基复合材料及摩擦磨损性能[J].金属学报,2001(03):315-320.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%