为提高TA1表面的耐磨性能,在TA1表面采用化学气相沉积(CVD)表面处理.用X射线衍射的方法测定了改性层的物相,使用显微硬度计测定了改性层和基体的硬度,在往复式滑动磨损试验机上进行磨损试验,通过扫描电子显微镜分析磨痕形貌.结果表明,TA1经过CVD处理,表面由α-Ti、Ti2N及TiN组成,显微硬度为989hV0.025.干摩擦条件下,经化学气相沉积处理的TA1材料的表面改性层的耐磨性得到了明显提高.
参考文献
| [1] | 黄虹.钛及其合金的非航空航天用途[J].稀有金属与硬质合金,2001(03):46-49. |
| [2] | Kathy Wang .The use of titanium for medical applications in the USA[J].Materials Science and Engineering,1996,213:134-137. |
| [3] | Wen C E;Yamada Y;Shimojima K .Processing and mechanical properties of autogenous titanium implant materials[J].Materials in Medicine,2002,13:397-401. |
| [4] | Buccioni E. .Processing-structure-adhesion relationship in CVD diamond films on titanium substrates[J].Diamond and Related Materials,1999(1 Jan):17-24. |
| [5] | Heinrich G;Grogler T;Rosiwal S M et al.CVD diamond coated titanium alloys for biomedical and aerospace applications[J].Surface and Coatings Technology,1997,94-95(514-520) |
| [6] | 阎洪.化学气相沉积层的技术和应用[J].稀有金属与硬质合金,1999(03):57-62. |
| [7] | 张菁 .化学气相沉积发展趋势[J].表面技术,1996,25(02):1-3. |
| [8] | 温诗铸;黄平.摩擦学原理[M].北京:清华大学出版社,2002:305-310. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%