利用扫描电子显微镜(SEM)对试片表面浸锌后质量优秀与低劣的锌合金层的微观形貌进行了比较,观察了不同浸锌时间及温度所对应的锌合金层的微观形貌,利用能谱仪(EDS)定量测定了锌合金层组成成分,利用X射线荧光能谱(XRF)定量测定了不同浸锌时间的锌合金层组成成分及膜厚.研究了锌舍金层表面明度、电位、膜重随浸锌时间的变化,膜重随浸锌温度的变化及浸锌后的试片在3.5%NaCl溶液中塔菲尔极化曲线,定性测定了试片浸锌后镀层的结合力.结果表明:锌合金层质量的好坏直接关系到镀层与基体的结合力,在浸锌合金过程中适合的参数可以间接表征锌合金层的质量.
参考文献
| [1] | Sharma A K;Bhojaraj H .Electroless nickel and gold plating on titanium alloys for space applications[J].Metal Finishing,1992,90(07):23. |
| [2] | 弗利德里克·A·洛温海姆;北京航空学院.现代电镀[M].北京:机械工业出版社,1974:712-719. |
| [3] | Robertson S G;Ritchie I M .The role of iron( Ⅲ ) and tartrate in the zincate immersion process for plating aluminium[J].Journal of Applied Electrochemistry,1997,27:799-804. |
| [4] | Monteiro F J .Surface Engineering[J].Surface and Interface analysis,1990,6(04):287. |
| [5] | Monteiro F J;Barbosa M A .Pretreatments to improve the adhesion of electrodeposits on aluminium[J].Surface and Interface Analysis,1991,17(07):519-528. |
| [6] | Williams;Barry.Gyanide containing pretreatment processes for plating on aluminum and its alloys: Are they really necessary?[A].,1999:533-539. |
| [7] | Pearson T;Wake S .Verbesserungen bei der vorbehandlung yon aluminium als substratfuerdie galvanische abscheidung[J].Galvanotechnik,2000,91:3054-3061. |
| [8] | 毛祖国,曾月莲,何杰.高硅铝合金电镀工艺[J].材料保护,2001(07):29-30. |
| [9] | 杨中东,李长业,李国喜,王毓民.铝硅合金铸造工艺品装饰镀金工艺[J].电镀与涂饰,2003(03):4-6,13. |
| [10] | 华树芳.压铸铝合金枪黑色电镀工艺[J].电镀与涂饰,2003(03):11-13. |
| [11] | 罗耀宗.铝合金电镀前处理新工艺[J].电镀与涂饰,2003(03):55-56. |
| [12] | 吴敏,孙勇.铝及其合金表面处理的研究现状[J].表面技术,2003(03):13-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%