对常温和低温下铝的阳极氧化效果进行了比较,解释了所获得的氧化膜在厚度和硬度上不同的现象.试验以硫酸为电解液,分别在25℃和(3±1)℃下对铝进行阳极氧化.结果发现3℃下获得的氧化膜的硬度约是25℃下获得的1.5倍,而且膜的厚度也有所增加.扫描电镜发现这两个温度下得到的氧化膜形貌大不相同.25℃下所得氧化膜的孔呈百合花状,口大而底窄,孔径达到2μm.而3℃下所得氧化膜呈立体网络结构,有如桦树叶的堆积,空隙在200nm左右.可见,前者有利于染色,后者有利于提高硬度.
参考文献
| [1] | 郭红霞.铝及铝合金着色工艺[J].表面技术,2004(01):59-60. |
| [2] | 朱祖芳.建筑铝型材的表面处理技术现况及发展趋势[J].电镀与涂饰,2005(04):14-17. |
| [3] | J. R. Morlidge;P. Skeldon;G. E. Thompson;H. Habazaki;K. Shimizu;G. C. Wood .Gel formation and the efficiency of anodic film growth on aluminium[J].Electrochimica Acta,1999(14):2423-2435. |
| [4] | G. Patermarakis .Development of a theory for the determination of the composition of the anodizing solution inside the pores during the growth of porous anodic Al_2O_3 films on aluminium by a transport phenomenon analysis[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,1998(1/2):25-41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%