利用定量金相分析、显微硬度测试、压痕断裂试验、结合强度测试和摩擦磨损试验,通过正交设计试验对等离子喷涂纳米结构Al2O3-13%TiO2(AT13)基陶瓷涂层的工艺进行了优化.分析了工艺参数、微观结构、力学性能之间的关系,提出了喷涂工艺图的建立方法,建立了相应的三维关系图.通过该工艺图可确定各个性能最优的工艺参数范围.
参考文献
| [1] | Sarikaya O .Effect of some parameters on microstructure and hardness of alumina coatings prepared by the air plasma spraying process[J].Surface & Coatings Technology,2005(2/3):388-393. |
| [2] | Tomaszek R;Pawlowski L;Zdanowski J;Grimblot J;Laureyns J .Microstructural transformations of TiO2, Al2O3+13TiO(2) and Al2O3+40TiO(2) at plasma spraying and laser engraving[J].Surface & Coatings Technology,2004(2/3):137-149. |
| [3] | Goberman D;Sohn Y H;Shaw L et al.Microstructure development of Al2O3-13%TiO2 plasma sprayed coatings derived from nanocrystalline powders[J].Acta Materialia,2002,50:1141-1152. |
| [4] | E. H. Jordan;M. Gell;Y. H. Sohn;D. Goberman;L. Shaw;S. Jiang;M. Wang;T. D. Xiao;Y. Wang;P. Strutt .Fabrication and evaluation of plasma sprayed nanostructured alumina-titania coatings with superior properties[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1):80-89. |
| [5] | 冯拉俊,惠博,梁天权.等离子喷涂NiAl-Al2O3梯度陶瓷涂层的性能研究[J].表面技术,2005(02):15-16,19. |
| [6] | 肖正伟,曾振欧,赵国鹏.纳米TiO2涂层在低碳钢上的防腐蚀性能[J].电镀与涂饰,2006(12):33-35,45. |
| [7] | 王海军.热喷涂实用技术[M].北京:国防工业出版社,2006:30-31. |
| [8] | 汤文博,孙玉福,陶玲.等离子喷涂Al2O3陶瓷涂层的冲蚀磨损特性[J].表面技术,2002(04):15-16,20. |
| [9] | 浦红,杨峥,陈斌.用计算机图形处理软件定量分析SEM图像[J].物理测试,2004(01):30-32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%