为了达到改善铝合金表面硬度低、耐磨耐蚀性差的目的,采用脉冲电源微弧氧化技术在硅酸钠电解液中在铝合金表面原位生长陶瓷膜.讨论氧化时间和电流密度对微弧氧化成膜厚度的影响.用数字式覆层测厚仪测量膜厚,扫描电子显微镜和X射线衍射分析膜层显微结构和相组成.结果表明:氧化时间越长,膜层越厚,但是30min以后不再增厚,电流密度越大,膜层越厚;陶瓷层表面有微孔产生,膜层与基体结合紧密,膜层由致密层、过渡层和疏松层组成,致密层厚且致密;氧化膜由γ-Al2O3、mullite莫来石(3Al2O3·2SiO2)和AlO相组成.
参考文献
| [1] | 刘静安,盛春磊.铝及铝合金加工材料的研制与开发趋向[J].铝加工,2005(04):37-40. |
| [2] | W. ZHANG;N. BAY .Cold Welding — Theoretical Modeling of the Weld Formation[J].Welding Journal,1997(10):417s-420s. |
| [3] | 侯亚丽,刘忠德.微弧氧化技术的研究现状[J].电镀与精饰,2005(03):24-28. |
| [4] | 张恒华 .有色金属表面微弧氧化技术[J].热处理,2008,23(02):5-8. |
| [5] | Mecuson, F;Czerwiec, I;Belmonte, T;Dujardin, L;Viola, A;Henrion, G .Diagnostics of an electrolytic microarc process for aluminium alloy oxidation[J].Surface & Coatings Technology,2005(1/4):804-808. |
| [6] | Sundararajan G.;Krishna LR. .Mechanisms underlying the formation of thick alumina coatings through the MAO coating technology[J].Surface & Coatings Technology,2003(2/3):269-277. |
| [7] | H.Y. Zheng;Y.K. Wang;B.S. Li .The effects of Na_2WO_4 concentration on the properties of microarc oxidation coatings on aluminum alloy[J].Materials Letters,2005(2/3):139-142. |
| [8] | 郭宝刚,梁军,田军,刘惠文,周金芳,徐洮.阳极电压对钛合金微弧氧化膜性能的影响[J].电镀与精饰,2005(03):1-4. |
| [9] | 赵晴,胡勇,杜楠.氧化时间对MB8镁合金微弧氧化膜的影响[J].航空材料学报,2007(06):55-58. |
| [10] | 李克杰,李全安.合金微弧氧化技术研究及应用进展[J].稀有金属材料与工程,2007(z3):199-203. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%