室温下,以Ce(NO3)3为主盐、KMnO4为氧化剂、氟化物为成膜促进剂在AZ91镁合金表面制备了Ce-Mn复合转化膜,分析了化学转化处理不同时间形成的转化膜的微观形貌和成分,研究了转化膜的耐腐蚀性能.结果表明:氟化物的加入可实现室温下快速成膜,膜层主要由Al,Ce,Mn和O元素组成,宏观上完整均匀,但存在微观裂纹;处理2 min所得的转化膜表现出较好的耐腐蚀性能,其自腐蚀电流密度比镁合金基材降低了1个数量级.最后,探讨了成膜机制及膜层的耐蚀机理.
参考文献
| [1] | 黄海军,韩秋华,王瑞权,申乐,刘明伟,赵海静.镁及镁合金研究动态与发展展望[J].中国铸造装备与技术,2010(01):1-5. |
| [2] | Amy L. Rudd;Carmel B. Breslin;Florian Mansfeld .The corrosion protection afforded by rare earth conversion coatings applied to magnesium[J].Corrosion Science,2000(2):275-288. |
| [3] | Dabala M.;Brunelli K.;Napolitani E.;Magrini M. .Cerium-based chemical conversion coating on AZ63 magnesium alloy[J].Surface & Coatings Technology,2003(2/3):227-232. |
| [4] | Scholes FH;Soste C;Hughes AE;Hardin SG;Curtis PR .The role of hydrogen peroxide in the deposition of cerium-based conversion coatings[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(4):1770-1780. |
| [5] | 张永君,严川伟,王福会.Mg及Mg合金表面稀土转化处理及其耐蚀性研究[J].腐蚀科学与防护技术,2001(z1):467-470. |
| [6] | 李凌杰,雷惊雷,于生海,田钰靖,蒋齐全,潘复生.镁合金铈转化膜的形成及表征[J].中国稀土学报,2007(06):736-740. |
| [7] | 钟丽应,曹发和,施彦彦,文强,张昭,张鉴清.AZ91镁合金表面铈基稀土转化膜的制备及腐蚀电化学行为[J].金属学报,2008(08):979-985. |
| [8] | 杨在兴,霍宏伟,王艳,付雅君,曹中秋.AZ91D镁合金表面铈转化膜成膜工艺及其耐腐蚀性的研究[J].腐蚀科学与防护技术,2009(02):200-202. |
| [9] | 杨潇薇,王桂香,董国君,龚凡.H2O2对AZ 31镁合金稀土转化膜的影响[J].电镀与环保,2009(05):35-38. |
| [10] | 陈东初,吴桂香,李炜常,李文芳,梁奕清.AZ91D镁合金无铬铈盐转化膜的正交试验研究[J].轻合金加工技术,2007(06):43-47,56. |
| [11] | LIN C S;FANG S K .Formation of Cerium Conversion Coatings on AZ31 Magnesium Alloys[J].Journal of the Electrochemical Society,2005,152(02):54-59. |
| [12] | R. F. Zheng;C. H. Liang .Conversion coating treatment for AZ91 magnesium alloys by a permanganate-REMS bath[J].Materials and Corrosion,2007(3):193-197. |
| [13] | 张军军,李文芳,杜军.常温时添加剂对Ce-Mn转化膜的影响[J].华南理工大学学报（自然科学版）,2010(04):76-82. |
| [14] | 郭毅,鲁彦玲,杜仕国.镁合金表面稀土转化膜研究进展[J].表面技术,2009(04):63-65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%