采用等离子喷涂技术在AZ31镁合金表面制备Al2O3-13％TiO2陶瓷复合涂层,对涂层的微观组织进行了观察分析,测试了涂层的表面硬度.通过极化曲线和浸泡腐蚀试验,对比研究了镁合金基材及喷涂陶瓷涂层的试样在5％ NaCl溶液中的耐腐蚀性能.结果表明:涂层镁合金试样的硬度和耐腐蚀性优于基体镁合金,但当腐蚀液透过涂层孔隙时,反而会加剧镁合金的腐蚀.
参考文献
| [1] | M.K. Lei;P. Li;H.G. Yang;X.M. Zhu .Wear and corrosion resistance of Al ion implanted AZ31 magnesium alloy[J].Surface & Coatings Technology,2007(9/11):5182-5185. |
| [2] | 冯亚如,张忠明,徐春杰,郭学锋.AZ31镁合金表面等离子喷涂Al65Cu23Fe12涂层的研究[J].铸造技术,2006(02):160-162. |
| [3] | 贺定勇,耿丹丹,蒋建敏.镁合金表面电弧喷涂铝涂层在氯离子中的腐蚀行为[J].焊接,2007(03):24-28. |
| [4] | GELL M;JORDAN E H;SOHN Y H et al.Development and Implementation of Plasma Sprayed Nanostructured Ceramic Coating[J].Surface and Coatings Technology,2001,146/147:48-54. |
| [5] | LIN X H;ZENG Y;LEE S W et al.Charaterization of A lumina 23wt% Titania Coating Prepared by Plasma Spraying of Nanostructured Powder[J].Journal of the European Ceramic Society,2004,24(04):627-634. |
| [6] | 杨元政,刘正义,庄育智.等离子喷涂Al2O3+13%TiO2陶瓷涂层的组织结构及其耐磨性[J].功能材料,2000(04):390-392. |
| [7] | 叶宏,张津,孙智富,杨惠,詹捷.镁合金表面等离子喷涂纳米陶瓷涂层研究[J].武汉理工大学学报,2004(04):9-11. |
| [8] | 李莉,贺定勇,蒋建敏,李晓延.AZ31镁基体等离子喷涂NiAl粒子扁平行为研究[J].材料热处理学报,2010(06):150-154. |
| [9] | 宫文彪,李于朋,马凯,孙大千.镁合金等离子喷涂Al/Al_2O_3涂层的耐腐蚀性能[J].材料热处理学报,2009(06):164-168. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%