初步研究了锌铬膜工艺条件。首先初步确定了锌铬膜涂料中锌粉、铬酐和硼酸的含量，筛选出两种有效的还原剂R1和R2并初步确定了其含量。之后利用正交实验研究了锌铬膜涂料基本组成的最佳配比。最后筛选出添加剂A有效提高了锌铬膜的结合力。指出了锌铬膜工艺下一步研究的重点。
The technique of Zn-Cr coating was preliminary studied in this paper. Firstly, the contents of zinc powder, CrO3 and H3BO3 in the Zn-Cr coating paint were preliminary studied. The two kinds of reductant R1 and R2 were selected and the contents of them were determined. Then the optimum composition of the Zn-Cr coating paint was researched. At last, the additive A was selected to improve the adhesion of the coating. Further research efforts were pointed out.
参考文献
| [1] | Mulkin J .Dacromet-a new corrosion protection for fasteners[P].US:3671331,1972. |
| [2] | 孙贺民.锌铬膜--一种特殊的表面处理新技术[J].材料保护,1994(08):21. |
| [3] | 张伟明.达克罗--当今世界表面处理的高新技术[J].材料保护,1995(08):19. |
| [4] | 陈玲,李宁,谷云龙,周德瑞.达克罗技术的绿色特点及代镉镀层的研究[J].电镀与环保,2000(02):24-26. |
| [5] | 文光男.锌-铬水系涂层的研究[J].材料保护,1996(06):1. |
| [6] | 李宁.锌基烧结涂层基本工艺条件的探索[J].材料保护,1998(12):16. |
| [7] | 徐立冲;陈中兴;马志伟 等.锌铬膜的制备及耐蚀性的研究[J].腐蚀与防护,1998,19(03):108-110. |
| [8] | 文光男,刘希柏.锌基复合涂层的研究与设计[J].材料保护,1999(04):37-38. |
| [9] | 文光男.锌基涂层的电化学行为及防蚀机理[J].材料保护,1998(02):8. |
| [10] | 万德立,朱殿瑞,苏红军,陈祥利,詹德喜.锌铬膜涂覆工艺的研究[J].材料保护,1999(07):32-34. |
| [11] | Lonca M .Dacrotizing-an effective protection against corrosion[J].Finishing,1990,14(09):35-38. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%