在与电流平行的匀强磁场下电沉积制备镍-铁膜,并分析其显微组织.研究发现:匀强磁场可以细化树枝晶主轴,抑制粗大二次枝晶的生长,更强磁场(12 T)下主轴晶呈现出断裂趋势;强磁场使电沉积样品晶粒发生择优取向;磁致对流效应对镍-铁合金膜成分没有明显影响.

参考文献

[1] 迟广俊,冯钊永,赵瑾,姚素薇.纳米金属多层膜与多层纳米线的电化学制备及其表征[J].物理化学学报,2003(02):177-180.
[2] 王晨;陈俊明.磁场对金属腐蚀与电沉积的影响[J].腐蚀与防护,1991(12):165-171.
[3] Amblard J;Epelboin I;Froment M.Inhibition and nickel electrocrystallization[J].Journal of Applied Electrochemistry,1979(09):233-242.
[4] Epelboin I;Wiart R .Mechanism of the electrocrystallization of nickel and cobalt in acidic solution[J].Electochemical Science,1971,118(10):1577-1582.
[5] Gu Z H;Chen J;Olivier A et al.The magnetic field effect on the dynamics of the anodic dissolution of copper[J].Journal of The Electrochemical Society,1993,14(02):408-414.
[6] O'Reilly C;Hinds G;Coey J M D .Effect of a magnetic field on electrodeposition chronoamperometry of Ag,Cu,Zn and Bi[J].Journal of the Electrochemical Society,2001,148:C674-678.
[7] G. Hinds;J. M. D. Coey;M. E. G. Lyons .Influence of magnetic forces on electrochemical mass transport[J].Electrochemistry communications,2001(5):215-218.
[8] 程华.磁电解技术[J].现代化工,1991(02):54-63.
[9] Vitanov T;Popov S;Budevski E .Mechanism of electrocrystallization[J].Nuclear Tracks and Radiation Measurements,1974,121(02):207-211.
[10] O' Brien R N;Santhanam K S V .Magnetic field effects on the growth of the diffusion layer at vertical electrodes during electrodeposition[J].Electrochemical Science and Technology,1982,129(06):1266-1268.
[11] O. Devos;A. Olivier;J. P. Chopart;O. Aaboubi;G. Maurin .Magnetic field effects on nickel electrodeposition[J].Journal of the Electrochemical Society,1998(2):401-405.
[12] Matsushima H.;Nohira T.;Mogi I.;Ito Y. .Effects of magnetic fields on iron electrodeposition[J].Surface & Coatings Technology,2004(2/3):245-251.
[13] Nicholas Leventis;Muguo Chen;Xuerong Gao et al.Electrochemistry with stationary disk and ring-disk millielectrodes in magnetic fields[J].Journal of Physical Chemistry B,1998,102:3512-3522.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%