研发了一种无铅无镉的化学镀镍新工艺,以两种新型稳定剂复合使用替代铅和镉,确定稳定剂SY-2的最佳用量为4 mg/L镀液在6周期仍保持清澈透明,具有良好的稳定性;镀速在0～6周期之间为27～21 μm/h,镀层磷质量分数为5.6%～9.0%,所得镀层光亮、硬度高、孔隙率低,具有良好的结合力和耐腐蚀性.该工艺镀液稳定性和镀层性能在一定程度上已超过了有铅有镉工艺,完全可以作为含铅、镉化学镀镍的替代品.
参考文献
| [1] | 杜岱春.分析化学[M].上海:复旦大学出版社,1993:190-191. |
| [2] | 李宁.化学镀实用技术[M].北京:化学工业出版社,2004:482-487. |
| [3] | 屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:332-338. |
| [4] | 郭忠诚;杨显万.化学镀镍原理及应用[M].昆明:云南科学技术出版社,1998:53-56. |
| [5] | Namboodiri P N N;Prasad K V;Mathur P B .Role of stabilizers in electroless plating baths[J].TRANSACTIONS OF THE SAEST,1972,7(03):122-126. |
| [6] | Rozenblyum R G;Burakov M R;Yakov A A D .Use of stabilizers during chemical nickel plating[J].Zashchita Metallov,1971,7(03):351-353. |
| [7] | Lanzoni E;Martini C;Ruggeri R et al.Structure and corrosion behavior of electroless Ni coatings deposited from differrently stabilized baths[J].European Federation of Corrosion Publications,1997,20:232-243. |
| [8] | Kivel J;Sallo J S .The effect of thiourea on alkaline electroless deposition[J].Journal of the Electrochemical Society,1965,112(12):1201-1203. |
| [9] | Heber J;Egli A .Electroless nickel plating composition and method of depositing electroless nickel layer[P].TW 226382B,2005-01-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%