在Cr2O3涂层中加入不同含量的CeO2和SiO2 添加剂,通过涂层热震试验及对热震试验结果的计算分析表明,涂层的热震失效本质为热应力疲劳失效;在Cr2O3涂层中加入CeO2和SiO2,可显著提高涂层的临界热震温差范围△TC.采用CeO2作添加剂使涂层的热震抗力系数提高较多,而SiO2则更多地提高△TC.涂层在300℃温度下工作时,选用3.0%CeO2作添加剂,使之具有较好的综合性能;涂层在300～500℃范围内工作,采用3.0%～6.0% SiO2作添加剂,其抗热震性较好.
参考文献
| [1] | 曾汉民.高技术新材料要览[M].北京:中国科学技术出版社,1993:303. |
| [2] | Ding C X;Huang B T;Lin H L.Plasma-sprayed wear-resistant ceramic and cermet coating materials[J].Thin Solid Films,1984(18):485-493. |
| [3] | Leivo E M;Vippola M S;Sorsa P P A;Vuoristo P M J and Mantyl .Wear and corrosion properties of plasma sprayed Al2O3 and Cr2O3 coatings sealed by aluminum phosphates[J].Journal of Thermal Spray Technology,1997,6(02):205-210. |
| [4] | Richard C S;Lu J;Béranger G;Decomps F .Study of Cr2O3 coatings[J].Journal of Thermal Spray Technology,1995,4(04):342-352. |
| [5] | 李幕勤;马臣;邵德春;郭面焕.CeO2添加剂对ZrO2涂层抗热震性的影响[A].北京:机械工业出版社,1997:1-444;1-446. |
| [6] | Chen H C;Pfender E;Heberlein J .Plasma-sprayed ZrO2 thermal barrier coating doped with an appropriate amount of SiO2[J].Thin Solid Films,1998,315:159-169. |
| [7] | 徐滨士;朱绍华;刘世参;马世宁.表面工程与维修[M].北京:机械工业出版社,1996:3228. |
| [8] | 化学工业部化工机械研究院.腐蚀与防护手册[M].北京:化学工业出版社,1990:249. |
| [9] | 王引真,孙永兴,鄢君辉,郑修麟,阎国超.热障涂层热震失效寿命定量计算的研究[J].无机材料学报,1999(01):138-142. |
| [10] | 王引真 .[D].西安:西北工业大学,1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%