研究了氧乙炔火焰喷涂制备的Al2O3/TiO2-NiCrBSi阶梯热障涂层在水淬热冲击条件下的失效行为.结果表明,涂层的抗热冲击能力随梯度成分间隔的减小而增强,其失效是由于涂层层间裂纹和层内裂纹共同作用的结果.对于成分梯度化较好的涂层,层内裂纹扩展导致网状裂纹是失效的主要原因;层间成分间隔大,失效则是以层间裂纹的快速扩展而导致涂层整体剥落为主要原因;当成分间隔介于以上二者时,层内裂纹和层间裂纹共同作用,导致涂层以局部脱落或剥落形式失效.
参考文献
| [1] | Leibert C.H .[J].Thin Solid Films,1979,64:329. |
| [2] | 高发荣.热喷涂[M].北京:化学工业出版社,1992 |
| [3] | Watson J.W;S.R.Levina .[J].Thin Solid Films,1984,119:185. |
| [4] | G.McDonald et al.[J].Thin Solid Films,1980,73:491. |
| [5] | Fukumoto M et al.[J].Thermal Spraying,1993,30:20. |
| [6] | Musil J;Fiala J .[J].Surface and Coatings Technology,1992,52:211. |
| [7] | Levit M et al.[J].Materials Science and Engineering,1996,A206:30. |
| [8] | Ravichandran K.S .[J].Materials Science and Engineering,1995,A201:269. |
| [9] | Aihua W et al.[J].Surface and Coatings Technology,1993,57:169. |
| [10] | Soboley V.V et al.[J].Surface and Coatings Technology,1994,70:57. |
| [11] | 孟国文 等.[J].材料导报,1995,2:40. |
| [12] | John W.[J].Ceramic Industry,1993(06):60. |
| [13] | 周振丰.焊接冶金与金属焊接性[M].北京:机械工业出版社,1998 |
| [14] | Weiss W .[J].Surface and Coatings Technology,1995,71:201. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%