根据X射线应力测量原理建立复合材料基体屈服强度的试验方法，测量压铸态20vol% SiCw/Al复合材料中基体实际屈服强度。结果表明，复合材料中基体屈服强度明显高于单一基体材料，高位错密度及细小亚晶粒是复合材料基体强化的主要原因。
According to the principle of stress measurement by X-ray diffraction, the test method of matrix yield strength in composites was established. The actual yield strength of matrix in a 20vol%SiCw/Al composite was measured. The results show that, the matrix yield strength in the composite is obviously higher than that of single matrix material. The matrix strengthening in the composite is mainly due to high dislocation density and fine sub-gain.
参考文献
| [1] | M Taya;K E Lulay;D J Lloyd .[J].冶金材料学报,1991,39(01):73. |
| [2] | D Derby;JRWalker .[J].Scripta Metallurgica et Materialia,1988,22:529. |
| [3] | R J Arsenault;L Wang;C R Feng .[J].冶金材料学报,1991,39(01):47. |
| [4] | T W Clyne;P J Withers.Introduction to Metal Matrix Composites[M].Cambridge:Cambridge University Press,1993:84-86. |
| [5] | Ismail C Noyan;Jerome B Cohen.Residual Stress Measurement by Diffraction and Interpretation[J].Springer-Verlag,1989:117. |
| [6] | 孙正明;李家宝;王中光;吕毓雄.[J].理化检验-化学分册,1992(02):38. |
| [7] | C H Jiang;D Z Wang;C K Yao .J Mater Sci[J].Lett,1999,18:901. |
| [8] | H M Ledbetter;M W Austin .[J].Materials Science and Engineering,1987,89:53. |
| [9] | Z M Sun;J B Li;Z G Wang et al.[J].冶金材料学报,1992,40(11):2961. |
| [10] | T Christman;A Needleman;S Suresh .[J].Acta Materialia,1989,37(11):3029. |
| [11] | V Tvergaard .[J].冶金材料学报,1990,38(02):185. |
| [12] | Mary Vogelsang;R J Arsenault;R M Fisher .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17A:379. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%