通过观察高锰钢高温淬火和Si-Ca变质组织,指出高锰钢中的碳化物在高温淬火和变质处理过程中均能形成,并在一定条件下以团球状弥散分布于奥氏体晶粒内.此外,利用高温金相观察了高锰钢组织在加热或高温保温过程中的变化.发现碳化物溶入奥氏体的过程伴随着晶粒的长大.晶粒长大的方式是晶界迁移和大晶粒吞并小晶粒.表面组织层磨发现,表层碳化物溶解后,将留下小的孔洞.上述结果对开发不经热处理高锰钢及高锰钢热处理工艺的确定具有重要的参考价值.
参考文献
| [1] | Fucheng Z;Tingquan L .A study of friction-induced martensitic transformation for austenitic manganese steel[J].Wear,1997,212(02):195-198. |
| [2] | L. Ozler;A. Inan;C. Ozel .Theoretical and experimental determination of tool life in hot machining of austenitic manganese steel[J].International Journal of Machine Tools & Manufacture: Design, research and application,2001(2):163-172. |
| [3] | Janez Kopac .Hardening phenomena of Mn-austenite steels in the cutting process[J].Journal of Materials Processing Technology,2001(1/2):96-104. |
| [4] | W. S. OWEN;M. GRUJICIC .STRAIN AGING OF AUSTENITIC HADFIELD MANGANESE STEEL[J].Computer Methods in Applied Mechanics and Engineering,1998(1):111-126. |
| [5] | Ibrahim Karaman;H.Sehitoglu;Y.I.Chumlyakov .EXTRINSIC STACKING FAULTS AND TWINNING IN HADFIELD MANGANESE STEEL SINGLE CRYSTALS[J].Scripta materialia,2001(2):337-343. |
| [6] | Yanyao Jiang;Huseyin Sehitoglu .A model for rolling contact failure[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(1):38-49. |
| [7] | 施忠良,李绍雄,尹衍升.非热处理高碳高锰钢凝固研究及应用前景[J].应用科学学报,1995(01):63-68. |
| [8] | 李绍雄;何镇明;赵宇光.[J].金属学报,1991(10):384-388. |
| [9] | 陈希杰.高锰钢[M].北京:机械工业出版社,1989 |
| [10] | 李隆盛.铸钢及其熔炼[M].北京:机械工业出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%