采用真空自耗电极电弧熔炼制成钕氧化物颗粒增强钛基复合材料.分析了不同Nd含量的钕氧化物颗粒增强钛基复合材料的组织.测试了复合材料棒材的拉伸、热稳定性、持久和蠕变等力学性能.结果表明,Nd元素的加入能够明显地细化铸锭的低倍组织和β热处理棒材的显微组织.随着加入的Nd含量增加,钕氧化物颗粒尺寸增大,其体积分数也明显增多.Nd元素的加入对复合材料的力学性能有利,尤其是高温性能.
参考文献
| [1] | SASTRYSML;MESCHTER P J;O'NEAL J E .Structureandpropertiesofrapidlysolidifieddispersion-strengthenedtitaniumalloys:partⅠ,characterizationofdispersoiddistribution,structure,andchemistry[J].Metallurgical and Materials Transactions,1984,15(07):1451-1463. |
| [2] | SASTRYSML;PENG P J;BECKERMAN L P .Structureandpropertiesofrapidlysolidifieddispersion-strengthenedtitaniumalloys:partⅡ,tensileandcreepproperties[J].Metallurgical and Materials Transactions,1984,15(07):1465-1474. |
| [3] | SASTRYSML;PENG T C;O'NEAL J E.Design and development of advanced titanium alloys by rapid solidification technology[A].Oberursel:DGM,1985:397-404. |
| [4] | PENGTC;SASTRY S M L;O'NEAL J E.Rapid solidification processing of titanium alloys[A].Oberursel:DGM,1985:389-396. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%