研究了Co对Al-5%Fe(质量分数,下同)合金中Al3Fe相形貌的改善作用.合金中加入Co后可以在很大程度上改善Al3Fe相的形貌:未加Co的Al-5%Fe合金中的Al3Fe相大多为粗大的针状和片状;Co的加入量为0.2%时,Al3Fe相的形貌为小花朵状和细小条状;Co的加入量在0.2%～1.0%时, 细化效果较好,但尤以0.2%为最好,Co的加入量超过1.0%后,Al3Fe相开始略微粗化.在对Co元素的面扫描时发现其大多固溶在Al3Fe相内.X衍射分析发现,Co的量为0.2%和1.0%时合金中只存在Al和Al3Fe相,并未发现其它相.
参考文献
| [1] | ADAMMCLC;HOGAN L M .Thealuminum-ironeutecticsystem[J].Journal of the Australian Institute of Metals,1972,17:81-90. |
| [2] | SenkovON;FROES F H;STOLYAROV V V et al.MicrostructureandmicrohardnessofanAl-Fealloysubjectedtosevereplasticdeformationandaging[J].Nano-Structured Materials,1998,10(05):691-698. |
| [3] | Ohashi T.;Liu Y. .Internal friction of powder metallurgy (P/M) and ingot metallurgy (I/M) Al-Fe alloys at elevated temperature[J].Journal of Materials Science,1998(23):5589-5594. |
| [4] | YAN Hong-ge;CHEN Zhen-hua;KANG Zhi-tao .Formation regularity of phases in nanometer powders of Al-Fe alloy prepared by gas evaporation[J].Transactions of Nonferrous Metals Society of China,2000(5):653-655. |
| [5] | CHELLMANDJ;EKVALL J C;RAINEN R A .ElevatedtemperaturePMalloysforaircraftstructure[J].Metal Powder Report,1988,43(10):672-674. |
| [6] | 陆书荪;顾开道;郑来苏.有色铸造合金及熔炼[M].北京:国防工业出版社,1983 |
| [7] | SKJERPEP .IntermetallicphaseformedduringDC-castingofanAl-025wtpctFe-013wtpctSialloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1987,18(02):189-199. |
| [8] | 蒙尔多福;王祝堂;张振录;郑璇.铝合金的组织和性能[M].北京:冶金工业出版社,1988 |
| [9] | 杨江波.改善铝硅合金中铁相形态的措施[J].铸造,2000(08):454. |
| [10] | ADAMCMCL;HOGAN L M .CrystallographyoftheAl-Al3Feeutectic[J].Acta Materialia,1975,23:345-354. |
| [11] | 王家;黄积荣;林建生.金属的凝固及其控制[M].北京:机械工业出版社,1983 |
| [12] | 虞觉奇;易文质;陈邦迪.二元合金状态图集[M].上海:上海科学技术出版社,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%