采用扫描电镜原位拉伸和原位疲劳的方法,跟踪观察了人工植入Al2O3夹杂物的镍基粉末高温合金P/M Rene95中夹杂物导致裂纹萌生、扩展乃至断裂的过程,结果表明,无论是在单轴拉伸还是低周疲劳实验中,裂纹均首先萌生于脆性非金属夹杂物Al2O3处,大于一定尺寸的夹杂物,还会使该裂纹扩展成为导致合金断裂的主裂纹,从而大大降低合金的屈服强度、断裂强度及低周疲劳寿命.

参考文献

[1] ChangDR;KRUEGER D D;SPRAGUE R A.Superalloy powder processing,properties and turbine disk applications[A].New York:American Institute of Mining Metallurgical and Petroleum Engineers Inc,1984:245-273.
[2] KRUEGERDD;KISSINGER R D;MENZIES R G.Development and introduction of a damage tolerant high temperature nickel-base disk alloy, Rene′88DT[A].Pennsylvania:TMS,1992:277-286.
[3] SHAMLENCE;CHANG D R .EffectofinclusionsonlcflifeofhipplusheattreatedpowdermetalRene95[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1985,16(04):775-784.
[4] GrisonJandRemyL .Fatiguefailureprobabilityinapowdermetallurgyni-basesuperalloy[J].Engineering Fracture Mechanics,1997,57(01):41-55.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%