用原位生成法制备了球状VC颗粒增强不锈钢基复合材料.利用正交设计实验法,确定了制备该复合材料的最佳工艺.采用SEM,XRD等测试手段对复合材料的微观组织和相结构进行观察,证实了该复合材料基体上弥散分布着球状VC增强颗粒.讨论了浇注温度、保温时间等因素对形成VC增强颗粒的影响.实验验证了制备复合材料的最佳工艺.
参考文献
| [1] | 冯可芹,杨屹,王一三,沈保罗.铁基复合材料的制备技术与展望[J].机械工程材料,2002(12):9-11,23. |
| [2] | Pagounis E.;Lindroos VK. .Processing and properties of particulate reinforced steel matrix composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):221-234. |
| [3] | KOCZAK M J;PREMKUMAR M K .Emerging technology for the in-situ production of MMCs[J].Journal of The Minerals,Metals & Materials Society,1993,45(01):44-48. |
| [4] | 林涛,殷声,魏延平.原位反应在铸造法制备复合材料中的应用[J].材料导报,2000(01):30-31,64. |
| [5] | TSANG H T;CHAO C G;MA C Y .In situ fracture observation of a TiC / Ti MMC produced by combustion synthesis[J].Scripta Materialia,1996,35:8-13. |
| [6] | RAGHUNATH C .In situ technique for synthesizing Fe-TiCcomposites[J].Scripta Metallurgica et Materialia,1995,32(04):577-582. |
| [7] | FRANGE N;LEVIN L;SHNECK R et al.Iron-titanium-carbon system microstructure of titanium carbide ( TiCx )of various stoichiometries infiltrated with iron-carbon alloy[J].Scripta Materialia,1996,35(07):799-803. |
| [8] | 徐文雷,孙扬善,丁绍松.VCp和TiCp颗粒增强Fe3Al基合金的显微组织和力学性能[J].中国有色金属学报,2001(z1):150-153. |
| [9] | 锡淦;雷鹰;胡克俊.国外钒的应用概况[J].世界有色金属,2002(02):13-21. |
| [10] | 张欣苑;李凤春;曾广廷 .液相合成VC颗粒增强钢基表面复合材料研究[J].机械工程材料,1999,8(04):35-38. |
| [11] | 徐恒钧.冷却速度对Fe-C-V合金变质效果的影响[J].热加工工艺,1997(04):21. |
| [12] | 北京大学数学力学系概率统计组.正交设计法[M].北京:石油化学工业出版社,1976 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%