利用交流阻抗研究了微弧氧化电解液组分及浓度、电流密度、处理时间等对镁合金氧化陶瓷膜于3.5%(质量分数,下同)NaCl溶液中的耐蚀性的影响规律,同时对经不同浸泡时间时氧化陶瓷膜的耐蚀性进行了测试,以探讨氧化膜的耐蚀机理.研究得出:随着硅酸钠、氟化钠、甘油含量的增加以及微弧氧化电流密度的增大和处理时间的延长,微弧氧化陶瓷膜的耐蚀性均呈现出先增强后降低的趋势;经一定的腐蚀时间后,微弧氧化陶瓷膜的多孔层最终遭到破坏,而紧密层对防腐蚀起着至关重要的作用.
参考文献
| [1] | J.E. Gray;B. Luan .Protective coatings on magnesium and its alloys-a critical review[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):88-113. |
| [2] | H. Friedrich;S. Schumann .Research for a "new age of magnesium" in the automotive industry[J].Journal of Materials Processing Technology,2001(3):276-281. |
| [3] | MATHIEU S;RAPIN C;HAZAN J et al.Corrosion behaviour of high pressure die-cast and semi-solid cast AZ91D alloys[J].Corrosion Science,2002,44(12):2737-2756. |
| [4] | SONG G;ATRENS A;ST JOHN D et al.The anodic dissolution of magnesium in chloride and sulphate solutions[J].Corrosion Science,1997,39(10-11):1981-2004. |
| [5] | 郭洪飞,安茂忠,刘荣娟.镁及其合金表面化学转化处理技术[J].轻合金加工技术,2003(08):35-38,41. |
| [6] | 郭洪飞,安茂忠.镁及镁合金阳极氧化技术[J].轻合金加工技术,2003(12):1-5,22. |
| [7] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews;S. J. Dowey .Plasma electrolysis for surface engineering[J].Surface & Coatings Technology,1999(2/3):73-93. |
| [8] | Wenbin Xue;Chao Wang;Ruyi Chen .Structure and properties characterization of ceramic coatings produced on Ti-6Al-4V alloy by microarc oxidation in aluminate solution[J].Materials Letters,2002(6):435-441. |
| [9] | XUE W B;FENG Z W;CHEN R Y et al.Growth regularity of ceramic coatings formed bv microarc oxidation on Al-Cu-Mg alloy[J].Thin Solid Films,2000,372(1-2):114-117. |
| [10] | 薛文斌,邓志威,陈如意,张通和.LY12铝合金微弧氧化陶瓷膜的纳米压入研究[J].稀有金属材料与工程,2001(04):281-285. |
| [11] | 王亚明,蒋百灵,郭立新,雷廷权.磷酸盐系溶液中钛合金微弧氧化涂层生长与组织结构[J].中国有色金属学报,2004(04):548-553. |
| [12] | 姜兆华,李文旭,闫久春,李益民.微等离子体氧化法制备钛酸钡陶瓷膜[J].材料工程,2002(02):34-37. |
| [13] | 蒋百灵,张淑芬,吴国建,雷廷权.镁合金微弧氧化陶瓷层显微缺陷与相组成及其耐蚀性[J].中国有色金属学报,2002(03):454-457. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%