包混工艺是一种应用前景广泛的制备多孔炭/碳化物材料的工艺,包混粉体酚醛树脂含量可以有效地控制其多孔制品的成分和性能.本工作采用正交实验法研究了包混粉体中酚醛树脂含量与工艺参数(成分配比、热处理温度、热处理时间、老化处理温度、老化处理时间)之间的关系.结果表明,原料中酚醛树脂与硅粉质量比对包混粉体中酚醛树脂含量的影响最大.包混粉体中酚醛树脂的含量随着原料中酚醛树脂与硅粉质量比的增加而增加.当原料中酚醛树脂与硅粉的质量比为1:1,在45℃热处理时间120min,在45℃老化处理90min时,酚醛树脂能更有效、更均匀地包覆在硅粉表面.
参考文献
| [1] | MORANCAIS A;LOUVET F;SMITH D S et al.High porosity SiC ceramics prepared via a process involving an SHS stage[J].Journal of the European Ceramic Society,2003,23(11):1949-1956. |
| [2] | Nidia C. Gallego;James W. Klett .Carbon foams for thermal management[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(7):1461-1466. |
| [3] | Yu JS.;Chai GS.;Yoon SB. .Ordered uniform porous carbon by carbonization of sugars[J].Carbon: An International Journal Sponsored by the American Carbon Society,2001(9):1442-1446. |
| [4] | WANG Y X;TAN S H;JIANG D L .The effect of porous carbon preform and the infiltration process on the properties of reaction-formed SiC[J].CARBON,2004,42(8-9):1883-1839. |
| [5] | 徐世江.包混材料[J].炭素技术,2002(04):45-47. |
| [6] | 郭世柏,曲选辉,段柏华,何新波,秦明礼.钛合金粉末注射成形工艺参数的优化[J].材料工程,2004(11):32-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%