Nanostructured FeS-SiC coating was deposited by atmospheric plasma spraying (APS). The microstructure and phase composition of the coating were characterized with SEM and XRD, respectively. In addition, the size distribution of the reconstituted powders and the porosity of the coating have been measured. It was found that the reconstitiuted powers with sizes in the range of 20 to 80 μm had excellent flowability and were suitable for plasma spraying process. The assprayed FeS-SiC composite coating exhibited a bimodal distribution with small grains (30～80nm) and large grains (100～200nm). The coating was mainly composed of FeS and SiC, a small quantity of Fe1-x S and oxide were also found. The porosity of the coating was approximately 19 %.
参考文献
| [1] | YING Chun-zhu;CHUAN Xian -ding et al.Deposition and characterization of nanostructured WC-Co coating[J].Ceramics International,2001,27:669-674. |
| [2] | GOBERMAN D;SOHN Y H;SHAW L et al.Microstructure development of Al2O3-13 % TiO2 plasma sprayed coatings derived from nanocrystalline powders[J].Acta Materialia,2002,50:1141-1152. |
| [3] | Chen H.;Ding CX. .Nanostructured zirconia coating prepared by atmospheric plasma spraying[J].Surface & Coatings Technology,2002(1):31-36. |
| [4] | Lima RS.;Berndt CC.;Kucuk A. .Evaluation of microhardness and elastic modulus of thermally sprayed nanostructured zirconia coatings[J].Surface & Coatings Technology,2001(2/3):166-172. |
| [5] | You Wang;Stephen Jiang;Meidong Wang;Shihe Wang;T. Danny Xiao;Peter R. Strutt .Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2000(2):176-185. |
| [6] | CHEN Huang;ZHOU Xiaming;DING Chuanxian .Investigation of the thermomechanical properties of a plasma-sprayed nanostructured zirconia coating[J].Journal of the European Ceramic Society,2003,23:1449-1455. |
| [7] | Wang Hai-dou;Zhuang Da-ming;Wang Kun-lin .Comparison of the tribological properties of an ion sulfurized coating and a plasma sprayed FeS coating[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):321-327. |
| [8] | I. Ahmed;T. L. Bergaman .Thermal modeling of plasma spray deposition of nanostructured ceramics[J].Journal of Thermal Spray Technology,1999(2):315-322. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%