采用固气反应法制备铁氮化合物吸收剂,研究了工艺参数对产物组成、微波电磁参数的影响,既而确定产物中形成较高比例Fe4N的条件.结果表明:在360℃,3h反应条件下,产物中Fe4N质量分数最高,为45%;反应时间不变,产物介电常数随反应温度升高而增加,磁导率则相反;反应温度不变,产物磁导率随反应时间的增加而降低;产物经分散处理后制得的吸波材料反射率优于处理前,在11.67GHz处,可达-11.18dB.
参考文献
| [1] | 罗发,周万城,焦桓,赵东林.高温吸波材料研究现状[J].宇航材料工艺,2002(01):8-11. |
| [2] | 邢丽英.隐身材料[M].北京:化学工业出版社,2004 |
| [3] | 佐藤敏郎 .Basic investigation of a magnetic/dielectric multilayered transmission-line device[J].日本应用磁气学会志,1998,22(03):133-138. |
| [4] | JACK K H.The iron-nitrogen system:the preparation and the crystal structures of nitrogen-austenite and nitrogen-martensite[J].Proc Royal Soc A,1951(08):200-204. |
| [5] | Wu XL;Zhong W;Jiang HY;Tang NJ;Zou WQ;Du YW .Magnetic properties and thermal stability of gamma '-Fe4N nanoparticles prepared by a combined method of reduction and nitriding[J].Journal of Magnetism and Magnetic Materials,2004(1):77-81. |
| [6] | AKIMASA SAKUMA .Electronic and magnetic structure of iron nitride,Fe16 N2 (invited)[J].Applied Physics A:Materials Science & Processing,1996,79(08):5570-5575. |
| [7] | 周桂琴,连法增,高强.体状Fe3N和Fe2N化合物合成及其磁性研究[J].金属功能材料,1998(04):158. |
| [8] | LIU Jun-you;ZHANG Qi;YU Hang-jiang et al.Magnetic properties of the ising ferromagnetic iron nitride systerm[J].Journal of Magnetism and Magnetic Materials,2004,288:48-53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%