利用高温固相合成法在还原气氛中,合成了新型长余辉发光粉CaxSr1-xAl2O4:Eu 2+,并以硼酸盐体系玻璃B2O3-(Na,K)2O-XO和硅硼酸盐体系玻璃SiO2-B2O3-(Na,K)2O-X2O-XO 的低熔点玻璃作为载体,掺杂该发光粉合成了稀土蓄光发光玻璃.实验改进了合成发光玻璃的热处理方法,提出二阶段的热处理方案,确定了发光玻璃的最佳合成温度分别为820℃和880℃.并根据SEM结果,对两种发光玻璃的表面质量及发光强度进行了对比分析,发现合成的硼硅酸盐发光玻璃的稳定性和发光效果要好于硼酸盐发光玻璃.
参考文献
| [1] | Katsumata T.;Nabae T.;Komuro S.;Morikawa T.;Sasajima K. .Characteristics of strontium aluminate crystals used for long-duration phosphors[J].Journal of the American Ceramic Society,1998(2):413-416. |
| [2] | 陈清明,林元华,张中太,唐子龙.长余辉蓄光玻璃的制备及其性能研究[J].功能材料,2001(02):208-209. |
| [3] | TANG Z L;ZHANG F;ZHANG Z T et al.Luminescent properties of SrAl2O4:Eu,Dy material prepared by gel method[J].Journal of the European Ceramic Society,2000,20(12):2129-2132. |
| [4] | Lin YH.;Zhang F.;Tang ZL.;Chen QM.;Zhang ZT. .Preparation of the ultrafine SrAl2O4 : Eu,Dy needle-like phosphor and its optical properties[J].Materials Chemistry and Physics,2000(1):103-106. |
| [5] | Katsumata T.;Toyomane S.;Tonegawa A.;Kanai Y.;Kaneyama U.;Shakuno K. Sakai R.;Komuro S.;Morikawa T. .Characterization of trap levels in long-duration phosphor crystals[J].Journal of Crystal Growth,2002(Pt.1):361-366. |
| [6] | 李建宇.稀土发光材料及其应用[M].北京:化学工业出版社,2003 |
| [7] | 朱爱玲,廉世勋,李承志,毛向辉.用两种方法合成长余辉发光玻璃的对比研究[J].中国稀土学报,2002(06):625-629. |
| [8] | 西北轻工业学院.玻璃工艺学[M].北京:中国轻工业出版社,2000 |
| [9] | 吴柏诚.玻璃制造工艺基础[M].北京:中国轻工业出版社,1997 |
| [10] | 方俊鑫;陆栋.固体物理学[M].上海:上海科学技术出版社,1981 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%