综述了高强铝合金应力腐蚀的各种测试方法及其原理与应用情况,通过分析与评价各应力腐蚀性能测试方法的优缺点,可以看出,用单一方法评价铝合金的应力腐蚀性能及其机制是有局限性的,需要通过多种方法的相互印证进行综合分析.
参考文献
| [1] | B. Davo;A. Conde;J. de Damborenea .Stress corrosion cracking of B13, a new high strength aluminium lithium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(12):4113-4126. |
| [2] | Chang CH;Lee SL;Lin JC;Yeh MS;Jeng RR .Effect of Ag content and heat treatment on the stress corrosion cracking of Al-4.6Cu-0.3Mg alloy[J].Materials Chemistry and Physics,2005(2/3):454-462. |
| [3] | 杜则裕,陶勇寅,李云涛,李建军.国产X70管线钢的硫化氢应力腐蚀性能及其焊接性[J].焊接学报,2004(05):13-16,21. |
| [4] | 芦笙,陈静,林萍华.Cu-Al-Be形状记忆合金的应力腐蚀性能[J].腐蚀科学与防护技术,2002(05):267-270. |
| [5] | 吴荫顺;方智;何积铨.腐蚀试验方法与防腐蚀检测技术[M].北京:化学工业出版社,1996:104-123. |
| [6] | DESHAIS G;NEWCOMB S B .The influence of microstructure on the formation of stress corrosion cracks in 7xxx series aluminum alloys[J].Materials Science Forum,2000,331-337:1635-1640. |
| [7] | ASTM G44-1999.ASTM G44-1999.Standard practice for exposure of metals and alloys by alternate immersion in neutral 3.5% Sodium chloride solution[S]. |
| [8] | ASTM G64-1999.ASTM G64-1999.Standard classification of resistance to stresscorrosion cracking of heat-treatable aluminum alloys[S]. |
| [9] | ASTM G47-1998.ASTM G47-1998.Standard test method for determining susceptibility to stress-corrosion cracking of 2xxx and 7xxx aluminum alloy products[S]. |
| [10] | LEE Seong-min;Pyun Su-Ⅱ;Chun Young-gab .A critical evaluation of the stress-corrosion cracking mechanism in high-strength aluminum alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1991,22(06):2407-2414. |
| [11] | TSAI W T;DUH J B;YEH J J et al.Effect of pH on stress corrosion cracking of 7050-T7451 aluminum alloy in 3.5% NaCl solution[J].Corrosion,1990,46(05):444-449. |
| [12] | BRAUN R .Slow strain rate testing of aluminum alloy 7050 in different tempers using various synthetic environments[J].Corrosion,1997,53(03):467-474. |
| [13] | 乔利杰;王燕斌;褚武扬.应力腐蚀机理[M].北京:科学出版社,1993:15-17. |
| [14] | NAJJAR D;MAGNIN T;WARNER T J .Influence of critical surface defects and localized competition between anodic dissolution and hydrogen effects during stress corrosion cracking of 7050 aluminum alloy[J].Materials Science and Engineering A:Structure Materials:Properties Microstructure and Processing,1997,238(02):293-302. |
| [15] | TSAI T C;CHUANG T H .Role of grain size in the stress corrosion cracking of 7475 aluminum alloy[J].Mater Sei Eng A,1997,225(04):135-144. |
| [16] | TSAI T C;CHANG J C;CHUANG T H .Stress corrosion cracking of superplastically formed 7475 aluminum alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1997,28(06):2113-2121. |
| [17] | SINGH P M;LEWANDOWSKI J J .Effects of heat treatment on stress corrosion cracking of a discontinuously reinforced aluminum (DRA) 7xxx alloy during slow strain rate testing[J].Scripta Metallurgica et Materialia,1995,33(05):1393-1399. |
| [18] | PARKINS R N;SINGH P M .Stress corrosion crack comescence[J].Corrosion,1990,46(03):485-499. |
| [19] | TANGUY D;BAYLE B;DIF R et al.Hydrogen effects during SCC propagation of Al-5Mg in 30g/L NaCl solutions[J].Materials Science Forum,2000,331-337:1659-1664. |
| [20] | SPEIDEL M O .Stress corrosion cracking of aluminum alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1975,6(06):631-650. |
| [21] | DORWARD R C;HASSE K R .Flaw growth in high strength Al-Zn-Mg-Cu alloys exposed to stress corrosion environments[J].Corrosion,1978,34(04):386-395. |
| [22] | STALEY J T .Stress corrosion cracking of rapidly solidified magnesium-aluminum alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1975,8(03):631-657. |
| [23] | HASSE K R;DORWARD R C .Long-term marine atmospheric stress corrosion tests on high-strength AlZnMgCu alloys[J].Corrosion,1986,42(05):663-669. |
| [24] | DORWARD R C;HASSE K R .On tensile properties and SCC resistance of Al-Zn-Mg-Cu system alloys[J].Corrosion Science,1982,22(03):251-257. |
| [25] | MAITRA S .Determination of stress corrosion cracking of Al-Cu-Mg alloys by slow strain rate and alternate immersion testing[J].Corrosion,1981,37(01):98-103. |
| [26] | LI Xiao-mei;STARINK M J .Analysis of precipitation and dissolution in overaged 7xxx aluminum alloys using DSC[J].Materials Science Forum,2000,331-337:1071-1076. |
| [27] | RIONTINO G;ABIS S;MENGUCCI P .DSC investigation of natural ageing in high-copper AlCuMg alloys[J].Mater Sci Fornm,2000,331-337:1025-1030. |
| [28] | DEIASI R;ADLER P N .Calorimetric studies of 7000 series aluminum alloys:Ⅰ.Matrix precipitate characterization of 7075 Ⅱ.Comparison of 7075,7050,and RX720 alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1977,8(06):1177-1190. |
| [29] | ASTM E1004-2002.ASTM E1004-2002.Standard practice for determining electrical conductivity using the electromagnetic (eddy-current) method[S]. |
| [30] | J.S.Robinson;R.L.Cudd .Electrical conductivity variations in X2096, 8090, 7010 and an experimental aluminium lithium alloy[J].Materials Science Forum,2000(0):971-976. |
| [31] | COOPER K R;YOUNG L M;GANGLOFF R P et al.The electrode potential dependence of environment-assisted cracking of AA7050[J].Materials Science Forum,2000,331-337:1625-1634. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%