采用脉冲钨极氩弧钎焊使用CuSi3钎料对镀锌钢板进行连接.主要研究脉冲频率变化对接头界面组织和力学性能的影响.实验结果表明,当电弧脉冲频率由100Hz增加到2000Hz时,电弧钎焊熔池的搅拌和冲刷作用效果逐渐增强,促进了界面须状金属间化合物的破碎行为和熔池成分过冷区域的增加,使得钎料区域内部Fe5 Si3(Cu)强化相数量不断增多,弥散宽度变宽,由40μm增加到120μm,接头显微硬度最大值也相应增加,由175MPa增加到204 MPa.
参考文献
| [1] | 林三宝,宋建岭.电弧钎焊技术的应用及发展[J].焊接,2007(04):19-21,36. |
| [2] | 于治水,钱乙余,王凤江,祁凯,李晓泉.Cu基钎料电弧钎焊接头强度及断口分析[J].机械工程学报,2001(10):88-92. |
| [3] | BOUAIFI B.Low-heat process enhance jointing of coated sheet metals[J].Welding Journal,2003(01):26-31. |
| [4] | LUISA QUINTINO;GERVASIO PIMENTA;DANUT IORDACHESCU .MIG Brazing of Galvanized Thin Sheet Joints for Automotive Industry[J].Materials and Manufacturing Processes,2006(1/2):63-73. |
| [5] | YU Z S;LI R F;ZHOU F M et al.Joint evolution and strengthening mechanisms in arc brazed galvanized steels with Cu975i3 filler[J].Journal of Materials Science and Technology,2004,20(11):1479-1483. |
| [6] | LI R F;YU Z S;QI K et al.Growth mechanisms of interfacial compounds in arc brazed galvanized steel joints with Cu97Si3 filler[J].Journal of Materials Science and Technology,2005,21(04):483-487. |
| [7] | LACASTER J F.The physics of welding[M].Oxford:pergamon Press,1986 |
| [8] | 徐强,国旭明,王宗杰,杨成刚.双脉冲MIG焊对2219Al-Cu合金焊缝组织及性能的影响[J].热加工工艺,2004(10):3-5. |
| [9] | 单辉祖.材料力学(Ⅱ)[M].北京:高等教育出版社,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%