分别将热固性(FB)和热塑性(SFB)两种硼酚醛树脂按照质量比为0 :20,5:15,10:10,15:5 and 20:0的比例添加到EPDM基热绝缘材料中,研究了FB和SFB的质量比对热绝缘材料的力学性能、粘接性能和烧蚀性能的影响.结果显示,随着FB用量增加和SFB用量降低,绝热层材料的应力应变曲线逐渐变陡,交联密度、拉伸强度和粘接强度不断增加,抗烧蚀性能不断增强,但是其断裂伸长率却显著下降;而当FB和SFB树脂的重量比为10:10时,材料的综合性能均比较理想.
Two kinds of boron phenolic resin,thermosetting (FB) and thermoplastic (SFB),were added into EPDM based thermal insulation materials with a series of weight ratio of FB and SFB,such as 0:20,5:15,10:10,15:5 and 20:0.The effects of weight ratio of FB and SFB on the mechanical,bonding and ablative properties of the composites were investigated,respectively.The results showed that with the increasing of FB and the decreasing of SFB,the modulus of the composites increases,the crosslink density,the tensile strength and the bond strength of the composites are increasing gradually and its ablation resistance properties are improved continuously.However,the elongation decreases sharply with the weight ratio of FB and SFB increasing.Therefore,the optimal weight ratio of FB and SFB should be 10:10 to obtain the very thermal insulation material with the excellent comprehensive properties.
参考文献
| [1] | Jong Kyoo Park;Tae Jin Kang .Thermal and ablative properties of low temperature carbon fiber-phenol formaldehyde resin composites[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(12):2125-2134. |
| [2] | R. D. Patton;C. U. Pittman Jr.;L. Wang .Ablation, mechanical and thermal conductivity properties of vapor grown carbon fiber/phenolic matrix composites[J].Composites, Part A. Applied science and manufacturing,2002(2):243-251. |
| [3] | Harvey;Albert R;Ellertson et al.Fiber-reinforced rocket motor insulation[P].US 7070705,2006-07-04. |
| [4] | 高国新,郑元锁,巩红光,刘艺.腈纶/芳纶共混短纤维用量对柔性绝热层材料性能的影响[J].固体火箭技术,2005(03):212-215. |
| [5] | 高国新,郑元锁,孙捷,谭溢波,金志浩.有机纤维/EPDM绝热材料性能研究[J].固体火箭技术,2007(06):544-547. |
| [6] | Gao G X .Study on properties of insulating Material Reinforced with High Carbon Residue Rate Short Fibers[D].西安:西安交通大学,2005. |
| [7] | A R Bahramian;M Kokabi;M H N Famili.Ablation and thermal degradation behavior of a composite based on resol type phenolic resin:Process modeling and experimental[J].Polymer,2006(47):3661-3673. |
| [8] | 周瑞涛,郑元锁,孙黎黎,高国新,刘艺,巩红光.硼酚醛树脂/丁腈橡胶烧蚀材料性能研究[J].固体火箭技术,2007(02):159-162. |
| [9] | Zhang D T.Flame-retarding performance of high-temperature resistant FB phenolic resin[J].Thermosetting Resin,1996(03):51-56. |
| [10] | 张多太.FB耐高温阻燃热固性酚醛树脂接枝CTBN固化环氧树脂的性能研究[J].中国胶粘剂,2004(06):61-62. |
| [11] | 甘朝志.硼酚醛树脂的研制[J].贵州化工,1998(03):17-19. |
| [12] | M O Abdalla;A Ludwick;T Mitchell .Boron-modified phenolic resins for high performance applications[J].Polymer,2004,44:7353-7359. |
| [13] | J Gao;Y Liu;L Yang .Thermal stability of boron-containing phenol formaldehyde resin[J].Polymer Degradation and Stability,2004,63:19-22. |
| [14] | Jungang Gao;Liya Xia;Yanfang Liu .Structure of a boron-containing bisphenol-F formaldehyde resin and kinetics of its thermal degradation[J].Polymer Degradation and Stability,2004(1):71-77. |
| [15] | Wang, DC;Chang, GW;Chen, Y .Preparation and thermal stability of boron-containing phenolic resin/clay nanocomposites[J].Polymer Degradation and Stability,2008(1):125-133. |
| [16] | 张多太.新型耐高温阻燃树脂体系的性能及应用[J].宇航材料工艺,2001(05):19-23. |
| [17] | Zhang D T.Flame retardant property of high performance flame retardant FB phenolic resin[J].Aerospace Materials & Technology,1996(06):19-22. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%