通过液态浸渍结合热梯度化学气相渗透(TCVI)制备了碳化铪含量为2.5%(质量分数)的C/C (HfC-C/C)复合材料.利用split Hopkinson pressure bar (SHPB)装置,对HfC-C/C复合材料进行了不同载荷冲击损伤,采用氧乙炔火焰烧蚀法测定了复合材料的烧蚀性能,结合扫描电镜分析了冲击损伤对HfC-C/C复合材料烧蚀性能的影响.结果表明:动态冲击损伤对HfC-C/C复合材料线烧蚀率的影响不显著,而其质量烧蚀率随冲击载荷的增加而增加,且冲击载荷对HfC-C/C复合材料质量烧蚀率的影响存在有一个阈值,超过此值,材料的质量烧蚀率显著增加.
参考文献
| [1] | FITZER E .The future of carbon-carbon composites[J].Carbon,1987,25(02):163-190. |
| [2] | 李贺军.炭/炭复合材料[J].新型炭材料,2001(02):79-80. |
| [3] | Sufang Tang;Jingyi Deng;Shijun Wang;Wenchuan Liu;Ke Yang .Ablation behaviors of ultra-high temperature ceramic composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):1-7. |
| [4] | Wunder V.;Wegner A.;Emig G.;Arnold W.;Popovska N. .Multilayer coatings on CFC composites for high-temperature applications[J].Surface & Coatings Technology,1998(1/3):329-332. |
| [5] | AWASTHI S;WOOD J L .C/C composite materials for air craft brakes[J].ADVANCED CERAMIC MATERIALS,1988,3(05):449-451. |
| [6] | Keisuke Fujii;Eiichi Yasuda;Takashi Akatsu;Yasuhiro Tanabe .Effect of characteristics of materials on fracture behavior and modeling using graphite-related materials with a high-velocity steel sphere[J].International journal of impact engineering,2003(9):985-999. |
| [7] | KIM J K;MACKAY D B;MAI Y W .Drop-weight impact damage tolerance of CFRP with rubbermodified epoxy matrix[J].Composites,1993,24(06):485-494. |
| [8] | 李玉龙,郭伟国,徐绯,索涛.Hopkinson压杆技术的推广应用[J].爆炸与冲击,2006(05):385-394. |
| [9] | Zhang Z.X.;Kou S.Q. .Effects of loading rate on rock fracture: fracture characteristics and energy partitioning[J].International journal of rock mechanics and mining sciences,2000(5):745-762. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%