采用料浆包渗法,以SiO_2 粉为Si源,纯Al 粉为还原剂,NaF和NH_4Cl作为复合活化剂,Al_2O_3为惰性添加剂,蛋白质(鸡蛋清)为黏结剂,在Cu表面预先镀Ni层随后900℃,12h表面渗Si,制备渗Ni-Si层.研究了Al粉含量对渗Si层组织和力学性能的影响.结果表明:随铝粉含量的增加,渗层组织出现以下转变:Ni_3Si+Ni_(31)Si_(12)→Ni_(31)Si_(12)+Ni_2Si→Ni_3Si+NiAl,包渗过程由渗硅为主转变为渗铝为主;渗层硬度增加;摩擦系数由铝粉含量为10%(质量分数,下同)时的0.37降低到45%时的0.18,分别为纯铜的1/2,1/5.
参考文献
[1] | 孙远敬,岳立新,张雅玲.纯铜多元共渗及热处理工艺研究[J].煤矿机械,2006(06):1021-1022. |
[2] | Shi ZY.;Wang DQ. .Alumina particles in a copper matrix formed by aluminizing and internal oxidation[J].Journal of Materials Science Letters,1998(6):477-479. |
[3] | 张毅,田保红,陈小红,高颖颖,刘平,李炎.纯铜稀土催渗渗铝及其内氧化[J].铸造技术,2006(03):255-257. |
[4] | ASA K R;STAFFAN J .On the use of ceramic PVD coatings to replace metallic coatings in electrical contacts[J].Surface and Coatings Technology,1997,89(03):270-278. |
[5] | 甘正浩;毛志远;沈复初 等.铜的气体表面渗硅新工艺研究[J].材料科学与工程,1996,14(04):38-42. |
[6] | SHRIRAM S .Electrodeposition of nanocrystalline nickel a brief review[J].Tans IMF,2000,78(05):194-197. |
[7] | 刘森林,石子源,王德庆,丁志敏,赵键.纯铜表面镍硼合金涂层的制备[J].大连铁道学院学报,2005(04):62-65. |
[8] | 袁庆龙,苏永安,徐重.纯铜双层辉光离子渗镍研究[J].真空科学与技术学报,2004(01):40-42. |
[9] | 张跃飞,陈飞,苏永安,潘俊德,徐重.纯铜加弧辉光离子渗钛的研究[J].金属热处理,2002(04):27-28. |
[10] | Bateni MR.;Ashrafizadeh F.;Szpunar JA.;Drew RAL.;Mirdamadi S. .Oxidation behaviour of titanium coated copper substrate[J].Surface & Coatings Technology,2001(2/3):192-199. |
[11] | DATTA M K;PABI S K;MURTY B S et al.Thermal stability of nanocrystalline Ni silicides synthesized by mechanical alloying[J].Materials Science and Engineering A,2000,284:219-225. |
[12] | TAKASUGI T;WATANABE S;LZUMI O et al.Plastic flow of Ni_3(Si,Ti) single crystals[J].Acta Metallurgica,1989,37:3425-3436. |
[13] | TAKASUGI T;LZUMI O .Mechanical properties of recrystallized L1_2-type Ni_3 (Si,Ti) intermetallics[J].Journal of Materials Science,1991,26:1173-1178. |
[14] | Wang HM.;Wang CM.;Cai LX. .Wear and corrosion resistance of laser clad Ni2Si/NiSi composite coatings[J].Surface & Coatings Technology,2003(2/3):202-208. |
[15] | Cai LX;Wang HM;Wang CM .Corrosion resistance of laser clad Cr-alloyed Ni2Si/NiSi intermetallic coatings[J].Surface & Coatings Technology,2004(2/3):294-299. |
[16] | 王春敏,蔡良续,王华明.激光熔覆Ni-Si金属硅化物复合材料涂层显微组织与耐蚀性[J].中国有色金属学报,2002(z1):183-187. |
[17] | Yoon JK.;Kim GH.;Byun JY.;Lee JK.;Kim JS.;Hong KT. .Kinetics of chemical vapor deposition of Si on Ni substrates from a SiCl4-H-2 gas precursor mixture[J].Surface & Coatings Technology,2003(1):65-71. |
[18] | Yoon JK.;Byun JY.;Kim GH.;Lee JK.;Yoon HS.;Hong KT. .Formation process and microstructural evolution of Ni-silicide layers grown by chemical vapor deposition of Si on Ni substrates[J].Surface & Coatings Technology,2003(2/3):241-248. |
[19] | HE Y R;RAPP R A .Oxidation resistant Ge-doped silicide coating on Cr-Cr_2Nb alloys by pack cementation[J].Materials Science and Engineering A,1997,222(02):109-117. |
[20] | Levin L.;Katsman A. .On the problem of high-rate reactive diffusion[J].Materials Chemistry and Physics,1998(1):73-76. |
[21] | Xiang ZD.;Rose SR.;Datta PK. .Codeposition of Al and Si to form oxidation-resistant coatings on gamma-TiAl by the pack cementation process[J].Materials Chemistry and Physics,2003(2):482-489. |
[22] | 王红星,盛晓波,储成林,董寅生,林萍华.包渗时间对Cu表面Ni-Al涂层组织和性能的影响[J].材料工程,2008(08):52-56. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%