利用正交实验研究了硅烷偶联剂在镀锌板上的钝化工艺,采用KH-560对热镀锌板进行钝化处理.比较钝化膜与空白试样在5%NaCl溶液中的极化曲线、电化学交流阻抗谱,并通过盐水浸泡实验进一步验证了硅烷膜的耐蚀性能.结果表明:经硅烷钝化处理后的镀锌板,其腐蚀电流密度下降,极化电阻升高,硅烷膜抑制了镀锌板的腐蚀过程,其耐蚀性能优于空白试样,接近铬酸盐钝化膜的耐蚀性.
参考文献
| [1] | 王双红,刘常升,单凤君.镀锌板的有机硅烷钝化技术及其研究进展[J].腐蚀科学与防护技术,2008(01):35-37. |
| [2] | DIKINIS V;NIAURA G;REZAITE V .Formation of conversion silicate films on Zn and their properties[J].Transactions of the Institute of Metal Finishing,2007,85(02):87-93. |
| [3] | ARAMAKIK R.Preparation of chromate-free,self-healing polymer films containing sodium silicate on zinc pre-treated in a cerium (Ⅲ) nitrate solution for preventing zinc corrosion at scratches in 0.5M NaCl[J].Corrosion Science,2002(44):1375-1389. |
| [4] | 高红云,张招贵.硅烷偶联剂的偶联机理及研究现状[J].江西化工,2003(02):30-34. |
| [5] | Danqing Zhu;Wim J. van Ooij .Enhanced corrosion resistance of AA 2024-T3 and hot-dip galvanized steel using a mixture of bis-[triethoxysilylpropyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine[J].Electrochimica Acta,2004(7):1113-1125. |
| [6] | Montemor MF;Trabelsi W;Zheludevich M;Ferreira MGS .Modification of bis-silane solutions with rare-earth cations for improved corrosion protection of galvanized steel substrates[J].Progress in Organic Coatings: An International Review Journal,2006(1):67-77. |
| [7] | Montemor MF;Ferreira MGS .Analytical characterization of silane films modified with cerium activated nanoparticles and its relation with the corrosion protection of galvanised steel substrates[J].Progress in Organic Coatings: An International Review Journal,2008(3):330-337. |
| [8] | 李振中,温变英,谭英杰.PP/SiO2 纳米粒子复合材料中偶联剂用量的确定[J].华北工学院学报,2001(02):95-97. |
| [9] | 王雪明,李爱菊,李国丽,王威强,赵永辉.金属表面制备KH-560硅烷膜涂层的工艺研究[J].中国表面工程,2004(06):27-31. |
| [10] | 王雪明,李爱菊,李国丽,王威强.金属表面KH-560硅烷膜的粘结性能研究[J].机械工程材料,2005(11):8-10,66. |
| [11] | 吴海江,卢锦堂,陈锦虹.热镀锌钢表面硅烷膜耐蚀性能的初步研究[J].腐蚀与防护,2006(01):14-17. |
| [12] | 廖秀娟 .镀锌板的稀土钝化工艺的研究[D].武汉理工大学,2008. |
| [13] | 吴海江,卢锦堂,孔纲.热镀锌钢表面铈盐与硅烷处理后的耐蚀性能[J].腐蚀与防护,2007(07):353-356. |
| [14] | Cabral AM;Duarte RG;Montemor MF;Ferreira MGS .A comparative study on the corrosion resistance of AA2024-T3 substrates pre-treated with different silane solutions - Composition of the films formed[J].Progress in Organic Coatings: An International Review Journal,2005(4):322-331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%