研究了热循环过程中SnAgCu/Cu焊点界面金属间化合物的生长规律及焊点疲劳失效行为.提出了热循环条件下金属间化合物生长的等效方程以及焊点界面区不均匀体模型,并用有限元模拟的方法分析了热循环条件下焊点界面区的应力应变场分布及焊点失效模式.研究结果表明:低温极限较低的热循环,对应焊点的寿命较低.焊点的失效表现为钎料与金属间化合物的界面失效,且金属间化合物厚度越大,焊点中的累加塑性功密度越大,焊点越容易失效.
参考文献
| [1] | SHANGGUAN D K;刘建影;程兆年.无铅焊料互联及可靠性[M].北京:电子工业出版社,2008:35-40. |
| [2] | Andersson C.;Tegehall P.-E.;Andersson D. R.;Wetter G.;Liu J. .Thermal Cycling Aging Effect on the Shear Strength, Microstructure, Intermetallic Compounds (IMC) and Crack Initiation and Propagation of Reflow Soldered Sn-3.8Ag-0.7Cu and Wave Soldered Sn-3.5Ag Ceramic Chip Components[J].IEEE transactions on components and packaging technologies: A publication of the IEEE Components, Packaging, and Manufacturing Technology Society,2008(2):331-344. |
| [3] | John H.L.Pang;Luhua Xu;X.Q.Shi;W.Zhou;S.L.Ngoh .Intermetallic Growth Studies on Sn-Ag-Cu Lead-Free Solder Joints[J].Journal of Electronic Materials,2004(10):1219-1226. |
| [4] | DARVEAUX R;REICHMAN C;ISLAM N.Interface failure in lead free solder joints[A].Piscataway(NJ):IEEE,2006:906-917. |
| [5] | 李凤辉 .SnAgCu/Cu界面金属间化合物长大规律[D].北京工业大学,2007. |
| [6] | XU L H;PANG J H L.Intermetallic growth studies on SAC/ENIG and SAC/Cu-OSP lead-free solder joints[A].San Diego:IEEE,2006:1131-1136. |
| [7] | LIM G H;KWAN H F;SHI X Q.Intermetallic growth study on lead-free solder joint under thermal cycling and isothermal aging[A].Piscataway(NJ):IEEE,2003:578-583. |
| [8] | Luhua Xu;John H. L. Pang;Kithva H. Prakash;T. H. Low .Isothermal and Thermal Cycling Aging on IMC Growth Rate in Lead-Free and Lead-Based Solder Interface[J].IEEE Transactions on Components and Packaging Technologies,2005(3):408-414. |
| [9] | PANG J H L;PRAKASH K H;LOW T H.Isothermal and thermal cycling aging on IMC growth rate in Pb-free and Pb-based solder interfaces[A].Piscataway(NJ):IEEE,2004:109-115. |
| [10] | I. Dutta;P. Kumar;G. Subbarayan .Microstructural Coarsening in Sn-Ag-based Solders and Its Effects on Mechanical Properties[J].JOM,2009(6):29-38. |
| [11] | 李晓延,严永长,史耀武.金属间化合物对SnAgCu/Cu界面破坏行为的影响[J].机械强度,2005(05):666-671. |
| [12] | CHE F X;PANG J H L;XU L H.Investigation of IMC layer effect on PBGA solder joint thermal fatigue reliability[A].Piscataway(NJ):IEEE,2005:427-430. |
| [13] | CHE F X;PANG J H L;XU L H.IMC consideration in FEA simulation for Pb-free solder joint reliability[A].Piscataway(NJ):IEEE,2006:1018-1023. |
| [14] | RODGERS B;FLOOD B;PUNCH J.Experimental determination and finite element model validation of the anand viscoplasticity model constants for SnAgCu[A].Piscataway(NJ):IEEE,2005:490-496. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%