为避免高温钎焊条件下钎料与TiAl母材发生过度反应,设计了CoFe基和Fe基两种高温钎料.在1100℃/10min和1200℃/10min条件下进行了钎料对TiAl合金的润湿性实验,在1180℃/5min条件下进行TiAl合金的真空钎焊实验.结果表明,1200℃/10min条件下两种钎料在TiAl合金上润湿角约为30°.与Ni基钎料相比,两种钎料与TiAl的界面反应程度得到缓解.CoFe基钎料对应接头界面主要形成Ti3Al,TiAl,硅化物和(Ti,Cr)-B,而在宽度较窄的(约10μm)钎缝中心形成了富Cr固溶体.Fe基钎料接头组织基本与CoFe基钎料接头类似,区别在于钎缝中心为残余钎料区,宽度约40μm,主要为Fe基固溶体.残余钎料区附近生成TiB和TiB2两种硼化物,与CoFe基钎料接头中硼化物相比,数量明显增多.
参考文献
| [1] | M. F. ARENAS;V. L. ACOFF .Analysis of Gamma Titanium Aluminide Welds Produced by Gas Tungsten Arc Welding[J].Welding Journal,2003(5):(110-S)-(115-S)-0. |
| [2] | WU Huiqiang,Feng Jicai,He Jingshan,ZHOU Li.Microstructural characterization of electron beam welded joints of TiAl-based intermetallic compound[J].稀有金属（英文版）,2005(01):82-86. |
| [3] | Won-Bae Lee;Young-Jig Kim;Seung-Boo Jung .Effects of copper insert layer on the properties of friction welded joints between TiAl and AISI 4140 structural steel[J].Intermetallics,2004(6):671-678. |
| [4] | R.K. SHIUE;S.K. WU;S.Y. CHEN .Infrared brazing of TiAl intermetallic using pure silver[J].Intermetallics,2004(7/9):929-936. |
| [5] | R. K. Shiue;S. K. Wu;S. Y. Chen .Infrared brazing of TiAl intermetallic using BAg-8 braze alloy[J].Acta materialia,2003(7):1991-2004. |
| [6] | 韩明,康慧,曲平.Ti-15Cu-15Ni真空钎焊TiAl合金[J].航天制造技术,2004(04):22-24,32. |
| [7] | R.K. Shiue;S.K. Wu;Y.T. Chen .Infrared brazing of Ti_(50)Al_(50) and Ti-6Al-4V using two Ti-based filler metals[J].Intermetallics,2008(9):1083-1089. |
| [8] | 陈波,熊华平,毛唯,程耀永,谢永慧.TiAl基合金的钎焊研究[C].2004航空航天焊接国际论坛论文集,2004:375-378. |
| [9] | 熊华平;毛唯;陈波.TiAl基合金连接技术的研究进展[J].航空制造技术,2008(25):108-112. |
| [10] | MIEDEMA A R;BOER F R;BOOM R et al.Model predictions for the enthalpy of formation of transition metal alloys[J].CALPHAD-Computer Coupling of Phase Diagrams and Thermochemistry,1977,1:353-359. |
| [11] | 陈波;熊华平;毛唯.Ti3Al基合金的高温钎焊探索研究[A].郑州:中国焊接学会钎焊及特种连接专业委员会,2009:281-284. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%