采用球-盘磨损实验方法,研究了不同厚度2A12铝合金微弧氧化陶瓷层的摩擦学特性及其磨损性能,用SEM观察陶瓷层的表面形貌、截面显微组织以及磨损后的形貌,XRD研究陶瓷层的相组成.研究表明,随氧化时间延长,样品表面膜厚度趋于均匀,界面处氧化膜变得比较平坦.陶瓷层主要由α-Al2O3和γ-Al2O3相组成,随氧化时间的延长、厚度增大,γ-Al2O3相在陶瓷层中的含量逐渐减少,而高温态、高硬度的α-Al2O3相的含量随氧化时间的延长逐渐提高,陶瓷层的平均硬度逐渐增大;未磨光、有疏松层的陶瓷层的磨损失重和磨损速率随微弧氧化时间的延长、厚度增大均增大,而磨光、去除疏松层的陶瓷层的磨损失重和磨损速率则均逐渐下降;磨痕的形状均为滑动方向上呈现片状鱼鳞、沟槽,为黏着磨损特征,磨痕未见裂纹.
参考文献
| [1] | 李均明,朱静,白力静.铝合金微弧氧化陶瓷层的磨损特性[J].材料保护,2005(01):27-29. |
| [2] | YEROKHIN A L;VOEVODIN A A;LYUBIMOV V V et al.Plasma electrolytic fabrication of oxide ceramic surface layers for tribotechnical purpose on aluminum alloys[J].Surface and Coatings Technology,1998,110(03):140-146. |
| [3] | Curran JA;Clyne TW .Thermo-physical properties of plasma electrolytic oxide coatings on aluminium[J].Surface & Coatings Technology,2005(2/3):168-176. |
| [4] | GNEDENKOV S V;KHRISANFOVA O A;ZAVIDNAYA A G et al.Production of hard and heat-resistant coatings on aluminum using a plasma micro-discharge[J].Surface and Coatings Technology,2000,123(01):24-28. |
| [5] | 陈宏,冯忠绪,郝建民,李波.负脉冲对铝合金微弧氧化的影响[J].长安大学学报（自然科学版）,2007(01):96-98. |
| [6] | Yerokhin AL;Shatrov A;Samsonov V;Shashkov P;Pilkington A;Leyland A;Matthews A .Oxide ceramic coatings on aluminium alloys produced by a pulsed bipolar plasma electrolytic oxidation process[J].Surface & Coatings Technology,2005(2/3):150-157. |
| [7] | 蒋百灵,白力静,蒋永锋.LY12铝合金表面氧化铝陶瓷层的生长过程[J].中国有色金属学报,2001(z2):186-189. |
| [8] | VOEVODIN A A;YEROKHIN A L;LYUBIMOV V V et al.Characterization of wear protective Al-Si-O coatings formed on Al-based alloys by micro-arc discharge treatment[J].Surface and Coatings Technology,1996,86-87:516-521. |
| [9] | 辛铁柱,赵万生,刘晋春.铝合金表面微弧氧化陶瓷膜的摩擦学性能及微观结构研究[J].航天制造技术,2005(04):5-8. |
| [10] | 陈飞,周海,万汉城,陈晨,吕反修.铝合金表面微弧氧化陶瓷层摩擦学性能的研究[J].热加工工艺,2006(24):40-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%