以ZrO(NO3)2·2H2O,Sm2 O3为原料,柠檬酸(C6H8O7·H2O)为整合剂,采用溶胶-凝胶工艺分别制备了Sm2 Zr2O7前驱体溶胶和Sm2Zr2O7粉体,将两者按比例球磨混合制备复合浆料;在ZrB2/SiC基体上铺Al2O3粉高温处理制备过渡层.采用浸渍提拉法在含过渡层的ZrB2/SiC基体上制备出了Sm2Zr2O7涂层.用X射线衍射仪(XRD)分析了Sm2Zr2O7粉体的物相,用场发射扫描电镜(SEM)对粉体、过渡层及涂层的微观形貌进行了表征.结果表明:1150℃保温2h可以制备出具有单一焦绿石结构的Sm2 Zr2O7粉体;采用烧结制度为0~1100℃,8℃/min,1100~1550℃,4℃/min,可以制备出平整均匀的Al2O3过渡层;前驱体Zr离子浓度为1.87mol/L,固含量为45%时,经三次浸涂可以制备出完整的Sm2Zr2O7涂层.

参考文献

[1] STANLEY R LEVINE;ELIZABETH J OP1LA;MICHAEL C HALBIG .Evaluation of ultra-high temperature ceramics for aeropropulsion use[J].Journal of a European Ceramic Society,2002,22:2757-2767.
[2] LEE K N;MILLER R A;JACOBSON N S.Environmental durability of mullite/SiC and mullite/YSZ coating/SiC Systems[A].,1995:1037-1044.
[3] Kang N. Lee;Dennis S. Fox;Jeffrey I. Eldridge .Upper Temperature Limit of Environmental Barrier Coatings Based on Mullite and BSAS[J].Journal of the American Ceramic Society,2003(8):1299-1306.
[4] XU Yue,YAN Zhaotong.Investigation on the preparation of Si/muilite/Yb2Si2O7 environmental barrier coatings onto silicon carbide[J].稀土学报(英文版),2010(03):399-402.
[5] 张红松,胡仁喜,徐强,王富耻,刘玲.La_2O_3,CeO_2掺杂Sm_2Zr_2O_7陶瓷制备及热物理性能[J].稀有金属材料与工程,2009(z2):735-738.
[6] 王铀,王亮.新型锆酸盐基热障涂层材料的研究进展[J].中国表面工程,2009(06):8-18.
[7] 徐强,刘燕,王敬栋,万春磊,潘伟,齐龙浩.Gd2Zr2O7与Al2O3的高温界面反应[J].稀有金属材料与工程,2005(z1):587-589.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%