采用氧化钇和氧化铝为原料,以氯化锂为熔盐,用熔盐法合成了钇铝石榴石(YAG)粉体.研究了合成温度、熔盐量对合成钇铝石榴石粉体的影响,并对熔盐法合成钇铝石榴石粉体的形成机理进行了分析.研究结果表明:在700℃即可合成钇铝石榴石晶体,但含有一定的中间相；随着合成温度的升高及熔盐比例的提高,可合成出品体发育良好的较纯钇铝石榴石粉体,钇铝石榴石品体的形成为溶解-析出机理.
参考文献
| [1] | 丁志立,陈嵩,韩杰才.以碳酸氢铵为沉淀剂制备纳米钇铝石榴石粉体[J].材料工程,2005(02):48-50. |
| [2] | 李长青,左洪波,张明福,孟松鹤,韩杰才,丁志立.固相反应法制备透明多晶YAG陶瓷[J].硅酸盐学报,2006(08):979-984. |
| [3] | Eugenio Caponetti;Stefano Enzo;Barbara Lasio;Maria Luisa Saladino .Co-precipitation synthesis of neodymium-doped yttrium aluminium oxides nanopowders: Quantitative phase investigation as a function of joint isothermal treatment conditions and neodymium content[J].Optical materials,2007(10):1240-1243. |
| [4] | 冯素雅;丁菲;林丙臣 等.溶胶-凝胶法制备YAG的若干影响因素[J].功能材料,2007,38:217-219. |
| [5] | Yen-Pei Fu .Preparation of Y_3Al_5O_(12):Eu powders by microwave-induced combustion process and their luminescent properties[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):233-236. |
| [6] | 蔡忠英 .钛酸盐粉体熔盐法制备及其机理研究[D].北京:北京科技大学,2007. |
| [7] | 李雪冬,朱伯铨,汪厚植.熔盐法在无机材料粉体制备中的应用[J].材料导报,2006(03):44-47. |
| [8] | 李桂芳,曹全喜,李双春,苏莎莎.硝酸盐热分解法制备Nd：YAG透明激光陶瓷[J].西安电子科技大学学报（自然科学版）,2007(05):835-838. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%