利用控溅射技术,通过改变溅射C靶电流工艺参数,在45#钢上制备出Cr/C和Cr/C/N复合镀层.用能谱仪(EDS),X射线衍射仪(XRD)、扫描电子显微镜(SEM)检测镀层的微观组织;用HX-1000型维氏显微硬度计、球-盘摩擦磨损试验机(POD)、光学显微镜(OM)测试镀层的力学性能.结果表明:随C靶电流增加,镀层微观结构都变得更加均匀和致密,硬度在变大,韧性在提高,耐磨性明显提高;所获C电流为1.2A的镀层有优异的摩擦磨损性能;Cr/C/N镀层综合力学性能优于Cr/C镀层.
参考文献
| [1] | 崔兰芳,孙永兴.耐磨自润滑材料的研究[J].聊城大学学报（自然科学版）,2009(01):62-67. |
| [2] | 胡志彪,李贺军,付前刚,陈强,王兰英.低摩擦系数固体润滑涂层研究进展[J].材料工程,2006(03):60-63,68. |
| [3] | 蒋百灵,苏阳.碳含量对磁控溅射Cr/C镀层摩擦磨损性能的影响[J].摩擦学学报,2008(02):123-127. |
| [4] | Y.L. Su;T.H. Liu;C.T. Su;T.P. Cho .Effect of chromium content on the dry machining performance of magnetron sputtered Cr_xC coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):188-197. |
| [5] | POLCAR T;PARREIRA N M G;NOVIAK R .Friction and wear behavior of CrN coating at temperatures up to 500℃[J].Surface and Coatings Technology,2007,201(16-17):5228-5235. |
| [6] | SADUMAN S .Influence of chromium carbide coating on tribological performance of steel[J].Materials & Design,2006,27(02):85-91. |
| [7] | Jun Zhou,Zhe Wu,Zhanhe Liu.Influence and determinative factors of ion-to-atom arrival ratio in unbalanced magnetron sputtering systems[J].北京科技大学学报（英文版）,2008(06):775-781. |
| [8] | Cooke KE.;Hamsphire J.;Southall W.;Teer DG. .The industrial application of pulsed DC bias power supplies in closed field unbalanced magnetron sputter ion plating[J].Surface & Coatings Technology,2004(0):789-794. |
| [9] | 蔡殉.现代薄膜材料与技术[M].上海:华东理工大学出版社,2007:240-264. |
| [10] | 高玉周 .耐磨梯度表面层的制备及其滑动摩擦学特性的研究[D].大连海事大学,2000. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%