用籽晶法制备了沿不同晶体取向凝同的镍基单晶高温合金试样,研究了单晶中枝晶形貌和一次枝晶臂距随凝固取向的变化规律.结果表明:凝同方向偏离[001]取向小于15°时,枝晶排列比较规则,一次枝晶臂距随偏离角度增大而减小;偏离角度为25°时,部分二次枝晶臂阻断了相邻一次枝晶干的生长,导致一次枝晶臂距增大.沿[011]和[111]取向凝固的单晶中由于分别存在2个和3个择优生长的枝晶干,发展出了复杂的枝晶形态.
参考文献
| [1] | CARON P;KHAN T.Evolution of Ni-based superalloys for crystal gas turbine blade applications[J].Aerospace Science and Technology,1999(03):513-523. |
| [2] | 胡壮麒,刘丽荣,金涛,孙晓峰.镍基单晶高温合金的发展[J].航空发动机,2005(03):1-7. |
| [3] | REED R C.The superalloys fundamentals and applications[M].New York:cambridge University Press,2006:128-130. |
| [4] | 胡汉起.金属凝固原理[M].北京:机械工业出版社,2000:142-146. |
| [5] | HUNT J D.Solidification and Casting of Metals[M].London:Metals Society,1977 |
| [6] | WILLS V A;MCCARTNEY D G .A comparative study of solidification features in nickel-base superalloys:microstructural evolution and microsegregation[J].Materials Science and Engineering,1991,145A(02):223-232. |
| [7] | VIJAYAKUMAR M;TEWARI S N;LEE J E et al.Dendrite spacings in directionally solidified superalloy PWA1480[J].Materials Science and Engineering,1991,132A:95-201. |
| [8] | MA D;MEYER M;VEHN TER.Solidification behaviour of Ni-base superalloy CMSX-6[J].Journal de Physique IV,1993(03):339-342. |
| [9] | 何国.晶体取向对镍基单晶高温合金枝状组织的影响[J].材料工程,1994(02):1. |
| [10] | 何国;李建国;毛协民 等.晶体取向对单晶高温合金一次枝晶间距的影响[J].金属学报,1995,31(07):310-314. |
| [11] | 刘金来,金涛,张静华,胡壮麒.晶体取向对镍基单晶高温合金铸态组织和偏析的影响[J].中国有色金属学报,2002(04):764-768. |
| [12] | 方建锋,田志凌,燕平,张晋远,郑毅.镍基单晶高温合金（001）和（011）晶面的定向切割[J].机械工程材料,2009(06):45-47. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%