以二氧化硅气凝胶为基体,二氧化钛为红外遮光剂,E玻纤为骨架制备出有一定压缩强度的隔热块体材料；分别测样品的压缩强度R、热导率λ和常温(25℃)体积电阻率ρ.结果表明:pH=8～9时,含水料浆的分散情况较好；经过730℃处理0.5h的样品,与美国材料与试验协会的标准ASTM C533-85比较,R值0.41MPa符合,密度D= 151kg·m-3较低；样品在常温和480℃时,常压下的热导率λn分别为0.036W·m-1·K-1和0.061W· m-1·K-1,低于或远低于一般隔热材料.同时系统研究了以水泥熟料为黏结剂、采用注浆成型-常温常压干燥制备隔热块体材料,原料和样品都无毒,制备工艺简单,成本低,容易实现产业化.
参考文献
| [1] | A. Soleimani Dorcheh;M. H. Abbasi .Silica aerogel; synthesis, properties and characterization[J].Journal of Materials Processing Technology,2008(1-3):10-26. |
| [2] | 邓忠生;张会林;魏建东 等.掺杂SiO2气凝胶结构及其热学特性研究[J].航空材料学报,1999,19(04):39-43. |
| [3] | 何飞,赫晓东,李垚.二氧化硅干凝胶的制备与结构分析[J].材料工程,2005(12):13-16. |
| [4] | 邹宁宇;鹿成滨;张德信.绝热材料应用技术[M].北京:中国石化出版社,2005:55-216. |
| [5] | 杨自春,陈德平.SiO2纳米多孔绝热材料的制备与绝热性能研究[J].硅酸盐学报,2009(10):1740-1743. |
| [6] | FRANK D;ZIMMERMANNA;STUHLER H G .Aerogelhaltiges verbundmaterial,verfahren zu seiner herstellung sowie seine verwendung[P].European Patent:0793626B1,1999-05-19. |
| [7] | 杨海龙,倪文,梁涛,徐国强,徐丽.硅酸铝纤维增强纳米孔绝热材料的制备与表征[J].材料工程,2007(07):63-66. |
| [8] | MITCHELL M B D;JACKSON J D J .Method of manufacturing a thermal insulation body[P].European Patent:1204617B1,2003-08-27. |
| [9] | 施维尔菲格F;兹梅尔曼A;沃尼尔J 等.含有气凝胶和粘结剂的复合材料,其制备方法及其应用[P].中国专利:1077556C,2002-01-09. |
| [10] | 王衍飞,张长瑞,冯坚,姜勇刚.SiO2气凝胶/短切石英纤维多孔骨架复合材料的制备与性能[J].硅酸盐学报,2009(02):234-237. |
| [11] | 高庆福,冯坚,张长瑞,冯军宗,武纬,姜勇刚.陶瓷纤维增强氧化硅气凝胶隔热复合材料的力学性能[J].硅酸盐学报,2009(01):1-5. |
| [12] | 金承黎;张洪彪;张蓉艳 等.一种常压干燥制备二氧化硅气凝胶复合材料的方法[P].中国专利:101318659A,2008-12-10. |
| [13] | 李世普.特势陶瓷工艺学[M].武汉:武汉理工大学出版社,2003:53-162. |
| [14] | Kim CY;Lee JK;Kim BI .Synthesis and pore analysis of aerogel-glass fiber composites by ambient drying method[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2008(0):179-182. |
| [15] | 王非,胡子君,陈晓红,宋怀河.莫来石纤维增强疏水SiO2气凝胶的制备[J].宇航材料工艺,2009(01):35-37. |
| [16] | 刘开平;梁庆宣 .水镁石纤维增强SiO2气凝胶隔热材料的制备方法[P].中国专利:1803602A,2006-07-19. |
| [17] | FESMIRE J E .Aerogel insulation system for space launch applications[J].Cryogenics,2006,46(2-3):111-117. |
| [18] | 哈钦森 K W;李 S;科宾 D R 等.二氧化钛的水热制备方法[P].中国专利:101668704A,2010-03-10. |
| [19] | GB/T 1964-1996.多孔陶瓷压缩强度试验方法[S]. |
| [20] | Xiao-kun Ma;Nam-Hee Lee;Hyo-Jin Oh;Jae-Woo Kim;Chang-Kyu Rhee;Kyoung-Soon Park;Sun-Jae Kim .Surface modification and characterization of highly dispersed silica nanoparticles by a cationic surfactant[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2010(1/3):172-176. |
| [21] | Pointeau I;Reiller P;Mace N;Landesman C;Coreau N .Measurement and modeling of the surface potential evolution of hydrated cement pastes as a function of degradation[J].Journal of Colloid and Interface Science,2006(1):33-44. |
| [22] | Liao, DL;Wu, GS;Liao, BQ .Zeta potential of shape-controlled TiO2 nanoparticles with surfactants[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2009(1/3):270-275. |
| [23] | R. Plonka;E. Mader;S. L. Gao .Adhesion of epoxy/glass fibre composites influenced by aging effects on sizings[J].Composites, Part A. Applied science and manufacturing,2004(10):1207-1216. |
| [24] | 黄红燕,邵忠财,王国营,艾红军.溶胶共沉淀法制备氧化锆氧化铝复合粉体[J].材料研究学报,2008(03):246-250. |
| [25] | Dweck J.;Coelho ACV.;Cartledge FK.;Buchler PM. .Hydration of a Portland cement blended with calcium carbonate[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2000(1/2):105-113. |
| [26] | 杨海龙,倪文,孙陈诚,胡子君,陈淑祥.硅酸钙复合纳米孔超级绝热板材的研制[J].宇航材料工艺,2006(02):18-22. |
| [27] | 隋良志;王兆国;姚春林.水泥工业耐火材料[M].北京:中国建材工业出版社,2005:81-82. |
| [28] | 师昌绪;李恒德;周廉.材料科学工程手册[M].北京:化学工业出版社,2004:7-177. |
| [29] | 王保国;刘淑艳;王新泉.传热学[M].北京:机械工业出版社,2009:18-240. |
| [30] | 威尔特 J R;威克斯 G E;威尔逊 R E.动量、热量和质量传递原理[M].北京:化学工业出版社,2005:146-159. |
| [31] | MEYAR J;SCHOLZ M;ROCHNIA M .Fumed silica[P].World Patent:2007/071526A1,2007-06-28. |
| [32] | 曾令可;曹建新;刘世明.SiO2气凝胶-硅酸钙复合纳米孔超级绝热材料导热系数的测定及绝热机理分析[J].材料工程,2009(z1):27-31. |
| [33] | 高庆福,张长瑞,冯坚,冯军宗,姜勇刚,武纬.氧化硅气凝胶隔热复合材料研究进展[J].材料科学与工程学报,2009(02):302-306,228. |
| [34] | 陈德方;黄伟.电工绝缘材料手册[M].北京:水利电力出版社,1974:5-6. |
| [35] | 胡兆斌.绝缘材料工艺学[M].北京:化学工业出版社,2005:1-2. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%