利用MDI-50、聚醚多元醇和3,3’-二氯-4,4’--二氨基-二苯基甲烷(MOCA)扩链剂制备了MDI-50型聚氨酯弹性体,研究了游离异氰酸酯基质量含量、聚醚多元醇相对分子质量对MDI-50聚氨酯弹性体力学性能的影响,采用示差扫描量热分析(DSC)、热重分析(TG)、红外光谱(FTIR)及力学性能等测试方法对MDI-50型聚氨酯弹性体的结构及性能进行了表征和分析,并与TDI-80型聚氨酯弹性体相比较.结果表明:MDI-50型聚氨酯弹性体的综合性能明显优于TDI-80型.MDI-50型弹性体的硬度、撕裂强度和抗拉强度都随预聚体游离-NCO质量含量的提高而增大,随聚醚多元醇软链段相对分子质量增大而减小,而断裂伸长率相反.
参考文献
| [1] | Buckley, C.P.;Prisacariu, C.;Martin, C. .Elasticity and inelasticity of thermoplastic polyurethane elastomers: Sensitivity to chemical and physical structure[J].Polymer: The International Journal for the Science and Technology of Polymers,2010(14):3213-3224. |
| [2] | Pukanszky B;Bagdi K;Tovolgyi Z;Varga J;Botz L;Hudak S;Doczi T;Pukanszky B .Nanophase separation in segmented polyurethane elastomers: Effect of specific interactions on structure and properties[J].European Polymer Journal,2008(8):2431-2438. |
| [3] | Khalid Mahmood Zia;Ijaz Ahmad Bhatti;Mehdi Barikani .XRD studies of polyurethane elastomers based on chitin/1,4-butane diol blends[J].Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides,2009(2):183-187. |
| [4] | 何成汉,刘平桂,赫丽华,宋江选,李齐方.端硅氧烷基聚氨酯/环氧树脂复合材料形态及热力学性能研究[J].材料工程,2010(11):60-65. |
| [5] | 区洁,田立颖,王新灵.软硬段对聚氨酯弹性体结构性能的影响[J].功能高分子学报,2010(02):160-165. |
| [6] | 徐海涛,郝爱友,杨勇,王炳凯.MDI-50在塑胶跑道中的应用研究[J].聚氨酯工业,2004(05):30-32. |
| [7] | 陈海良,陈伟,王强,孙杰.MDI-50在耐溶剂聚氨酯弹性体中的应用研究[J].化学推进剂与高分子材料,2006(06):52-53,60. |
| [8] | 金日光;华幼卿.高分子物理[M].北京:化学工业出版社,2000:8-12. |
| [9] | 山西省化工研究所.聚氨酯弹性体手册[M].北京:化学工业出版社,2001:105-114. |
| [10] | 李万捷,张腊,王志忠,和涛,郭健.煤沥青粉填充氯醋/聚氨酯复合材料的热特性[J].高分子材料科学与工程,2008(06):136-139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%