锌铝镁镀层钢板比普通的镀锌钢板具有更加优异的耐腐蚀性能,本研究利用热镀锌模拟器在实验室制备了热浸镀锌铝镁合金镀层钢板,利用扫描电子显微镜SEM观察了镀层表面及截面的微观组织,利用能谱EDS进行了微区成分分析；利用电子探针EPMA对镀层的表面及截面进行了元素分布分析,利用盐雾试验方法对锌铝镁镀层钢板的耐腐蚀性能进行了研究,利用X射线衍射分析了镀层及镀层盐雾试验腐蚀产物的物相组成.结果表明,热浸镀锌铝镁镀层钢板比普通镀锌板具有更加细致的组织,镀层主要由MgZn2与含Al富锌相构成的共晶相和MgZn2组成,另外还存在一些粒状富铝相和块状富锌相,Zn-Al-Mg镀层比普通镀锌板具有更强的耐腐蚀性能,最后分析了锌铝镁镀层钢板的耐盐雾腐蚀机理.
参考文献
| [1] | SPEER J G;ASSUNCAO F C R;MATLOCK D K et al.The "quenching and partitioning" process:background and recent progress[J].Materials Research,2005,8(04):417-423. |
| [2] | LI Y .Formation of nano-crystalline corrosion products on Zn Al alloy coating exposed to seawater[J].Corrosion Science,2001,43(09):1793-1800. |
| [3] | Rocco AM.;Nogueira TMC.;Simao RA.;Lima WC. .Evaluation of chromate passivation and chromate conversion coating on 55% Al-Zn coated steel[J].Surface & Coatings Technology,2004(2/3):135-144. |
| [4] | KONG F R;SANTHANAKRISHNAN S;LIN D CH et al.Modeling of temperature field and grain growth of a dual phase steel DP980 in direct diode laser heat treatment[J].Journal of Materials Processing Technology,2009,209(18- 19):59966003. |
| [5] | Corrosion behaviour of Zn-Al-Mg coated steel sheet in sodium chloride-containing environment[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(10):2355. |
| [6] | Jonathan Elvins;John A. Spittle;James H. Sullivan;David A. Worsley .The effect of magnesium additions on the microstructure and cut edge corrosion resistance of zinc aluminium alloy galvanised steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(6):1650-1658. |
| [7] | HIDESHI F;RIE K;HIROSHI I .Hot-dip Zn-5% Al alloy-coated steel sheets[J].JFE Technical Report,2009,14(12):41-45. |
| [8] | E. De Bruycker;Z. Zermout;B.C. De Cooman .Zn-Al-Mg Coatings: Thermodynamic Analysis and Microstructure Related Properties[J].Materials Science Forum,2007(Pt.2):1276-1281. |
| [9] | E. De Bruycker;B.-C. De Cooman;M. De Meyer .Experimental study and microstructure simulation of Zn-Al-Mg coatings[J].Revue de Metallurgie: Cahiers d'Informations Techniques,2005(7/8):543-550. |
| [10] | Komatsu A.;Izutani H. .Corrosion Resistance and Protection Mechanism of Hot-dip Zn-Al-Mg Alloy Coated Steel Sheet under Accelerated Corrosion Environment[J].鉄と鋼,2000(8):36-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%