以Mo粉、Si粉和C粉为原料,采用湿法混合和原位反应高温热压一次复合工艺制备了不同配比的SiCp/MoSi2复合材料,研究了该种工艺原位生成的SiC颗粒对MoSi2基体显微结构和室温力学性能的影响.结果表明:原位反应生成的适量SiC颗粒可以细化基体晶粒,改善其力学性能,与同样工艺下制备的纯MoSi2相比,含40vol%SiCp的SiCp/MoSi2复合材料室温抗弯强度是其3.4倍,含50vol%SiCp的SiCp/MoSi2复合材料室温断裂韧性是纯MoSi2的1.5倍;该种工艺的强化机制为细晶强化和弥散强化,韧化机制为细晶韧化.
参考文献
| [1] | Vasudevan A K;Petrovic J J .A Comparative overview of molydbenum disilicide composite[J].Materials Science and Engineering,1992,155A:1-17. |
| [2] | 马勤;杨延清;康沫狂 .MoSi2及其复合材料的应用及展望[J].材料导报,1997,11(02):61-64. |
| [3] | Yang J M;Jeng S M .Interface and mechanical behavior of MoSi2based composites[J].Materials Research,1991,6(03):505-513. |
| [4] | 金志浩,李世斌,高积强.MoSi2基复相材料的研究进展[J].西安交通大学学报,2001(02):199-202. |
| [5] | Costa e Silva A;Kaufman M J .In-Situ Formation of Alumina Coating in Niobium Toughened Mo (Si,Al)2[J].Scripta Metallurgica et Materialia,1994,31(07):8.53. |
| [6] | Costa e Silva A;Kaufman M J .Applications of In Situ Reaction to MoSi2-Based Materials[J].Materials Science and Engineering,1995,A195:75. |
| [7] | 马勤;杨延清;康沫狂 .原位技术在MoSi2基复合材料制备中的应用与发展[J].兵器材料科学与工程,1997,20(05):66. |
| [8] | 寇开昌,杨延清,艾云龙,陈彦,康沫狂.MoSi2-WSi2复合体系的自蔓延燃烧合成[J].稀有金属材料与工程,2000(03):190-192. |
| [9] | 张来启,孙祖庆,张跃,杨王玥,陈光南.原位SiC颗粒增强MoSi2基复合材料的显微组织和力学性能[J].金属学报,2001(03):325-331. |
| [10] | 张来启;孙祖庆 et al.Densification of MoSi2/SiCp composites and their microstructure[J].北京科技大学学报,1997,19(06):577-579. |
| [11] | 孙岚,潘金生,清华大学,北京.TiC颗粒增韧MoSi2基复合材料的力学性能[J].材料工程,2001(09):31-34. |
| [12] | 郜剑英,江莞,李建林,吴历斌.二硅化钼合金化及掺杂改性的研究进展[J].中国钼业,2003(04):22-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%