对比研究了放电等离子烧结(SPS)和真空烧结(VAS)平均粒径为160nm的WC-12Co硬质合金的组织和性能.研究结果表明:SPS烧结能使WC-12Co在较低温度、较短时间内完全致密化,烧结温度比真空烧结低250℃以上,烧结时间只有真空烧结的1/26.相对于真空烧结,SPS烧结的晶粒更细,硬度提高1.5%以上,抗弯强度提高12.6%以上.
参考文献
| [1] | Xu Wang;Zhigang Zak Fang;Hong Yong Sohn .Grain growth during the early stage of sintering of nanosized WC-Co powder[J].International Journal of Refractory Metals & Hard Materials,2008(3):232-241. |
| [2] | X. L. Shi;G. Q. Shao;X. L. Duan .Characterizations of WC-10Co nanocomposite powders and subsequently sinterhip sintered cemented carbide[J].Materials Characterization,2006(4/5):358-370. |
| [3] | XiaoLiang Shi;Hua Yang;Gangqin Shao .Nanoindentation study of ultrafine WC-l0Co cemented carbide[J].Materials Characterization,2008(4):374-379. |
| [4] | McCandish L.E;Bear K.H .Spray Conversion Process For TheProduction of Nanophase Composite Powders[P].US 9107244,1991-05-30. |
| [5] | 彭金辉;张世敏;张利波.等离子体活化烧结材料[M].昆明:云南科学技术出版社,2001:1-16. |
| [6] | 株洲硬质合金厂.硬质合金的生产[M].北京:冶金工业出版社,1974:249-258. |
| [7] | 李蔚,高濂,郭景坤,宫本大树,DIAZ DE LA TORRE Sebastian.放电等离子快速烧结纳米3Y-TZP材料[J].无机材料学报,1999(06):985-988. |
| [8] | 冯海波,周玉,贾德昌.放电等离子烧结技术的原理及应用[J].材料科学与工艺,2003(03):327-331. |
| [9] | 解迎芳,王兴庆,陈立东,李晓东,郭海亮.放电等离子烧结纳米硬质合金的研究[J].硬质合金,2003(03):138-142. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%