为了提高热作模具钢H13的性能,延长模具的使用寿命,对表面纳米化后的热作模具钢H13,在远低于传统渗硼温度的600℃下实施等离子低温渗硼试验.结果表明:表面纳米化后的H13钢在600℃和4～8h的渗硼处理后,表面确实形成了6～10μm厚度的渗硼层,且具有约为16GPa的极高硬度;4～8h的不同渗硼时间,对渗硼层厚度,成分含量及形貌结构变化有影响,实验证明了表面纳米化处理对低温渗硼层的形成起到必要和良好的促进作用.
参考文献
| [1] | 崔崑.国内外模具用钢发展概况[J].金属热处理,2007(01):1-11. |
| [2] | 刘劲松.模具渗硼工艺及其发展应用[J].模具制造,2002(07):54-56. |
| [3] | 姜祖赓;陈再枝;任民恩;张震亚.模具钢[M].北京:冶金工业出版社,1988:2-5. |
| [4] | 张洪奎,刘笑莲.国内热作模具钢发展概况[J].热处理,2003(02):52-58. |
| [5] | 潘晓华,朱祖昌.H13热作模具钢的化学成分及其改进和发展的研究[J].模具制造,2006(04):78-85. |
| [6] | 曹光明.H13热作模具钢的表面热处理[J].特殊钢,2005(01):34-37. |
| [7] | 胡金锁,郝敬敏,李治源,王莹.碳钢表面渗硼和激光热处理改性层的磨粒磨损性能和机理研究[J].摩擦学学报,2002(02):150-152. |
| [8] | Sen S.;Sen U.;Bindal C.;Ozbek I. .Mechanical behavior of borides formed on borided cold work tool steel[J].Surface & Coatings Technology,2001(2/3):173-177. |
| [9] | Lee SY.;Kim GS.;Kim BS. .Mechanical properties of duplex layer formed on AISI 403 stainless steel by chromizing and boronizing treatment[J].Surface & Coatings Technology,2004(0):178-184. |
| [10] | 徐滨士,欧忠文,马世宁.纳米表面工程基本问题及其进展[J].中国表面工程,2001(03):6-12. |
| [11] | 徐滨士,梁秀兵,马世宁,刘世参,乔玉林,朱胜.实用纳米表面技术[J].中国表面工程,2001(03):13-17. |
| [12] | 曹扬,陈光,颜银标.钢铁材料表面自身纳米晶化及其应用前景[J].钢铁研究学报,2005(02):1-6. |
| [13] | Tong W.P;Tao N.R;Wang Z.B;Lu J.Lu K.Nitriding iron at lower temperatures[J].Science,2003(01):299,686-688. |
| [14] | Z.B. Wang;J. Lu;K. Lu .Chromizing behaviors of a low carbon steel processed by means of surface mechanical attrition treatment[J].Acta materialia,2005(7):2081-2089. |
| [15] | 吴晓春,徐凌云,汪宏斌.表面机械研磨处理后H13钢的等离子渗硼研究[J].材料热处理学报,2007(z1):154-157. |
| [16] | Xu Lingyun;Wu Xiaochun;Wang Hong-bin.The modifying effect of surface nano-structured treatment on hot work steel H13[A].,2006:537-544. |
| [17] | 周玉;武高辉.材料分析测试技术[M].哈尔滨:哈尔滨工业大学出版社,2005 |
| [18] | 冯耀文.[J].金属热处理,1983(11):34. |
| [19] | 韩靖,盛光敏,胡国雄.金属材料表面自纳米化研究现状[J].材料导报,2007(z1):2-6. |
| [20] | Bindal C;Ucisik AH .Characterization of boriding of 0.3% C, 0.02% P plain carbon steel[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2007(1):90-94. |
| [21] | Nikitin I;Altenberger I;Maier HJ;Scholtes B .Mechanical and thermal stability of mechanically induced near-surface nanostructures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):318-327. |
| [22] | Oliver,W.C;Pharr,G.M .[J].Journal of Materials Research,1992,7(06):1564. |
| [23] | Oliver,W.C .[J].Journal of Materials Science,2001,16(11):3202. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%